D4.8 Th Zr2 Bartscher W, Rebizant J, Boeuf A, Caciuffo R, Rustichelli F, Fournier J, Kuhs W Journal of the Less-Common Metals 121 (1986) 455-460 Distribution of deuterium in the cubic Laves phases Th Zr2 Dx _cod_database_code 1008699 _database_code_amcsd 0016585 CELL PARAMETERS: 9.1120 9.1120 9.1120 90.000 90.000 90.000 SPACE GROUP: Fd3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 756.556 Density (g/cm3): 7.362 MAX. ABS. INTENSITY / VOLUME**2: 411.2372245 RIR: 18.189 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 16.85 9.83 5.2608 1 1 1 8 27.69 59.69 3.2216 2 2 0 12 32.59 100.00 2.7474 3 1 1 24 34.08 16.47 2.6304 2 2 2 8 43.28 2.79 2.0904 3 3 1 24 48.97 23.20 1.8600 4 2 2 24 52.16 8.08 1.7536 3 3 3 8 52.16 24.26 1.7536 5 1 1 24 57.19 23.55 1.6108 4 4 0 12 60.07 1.82 1.5402 5 3 1 48 64.70 8.93 1.4407 6 2 0 24 67.39 9.95 1.3896 5 3 3 24 68.28 5.35 1.3737 6 2 2 24 78.56 9.31 1.2176 6 4 2 48 81.06 5.42 1.1863 5 5 3 24 81.06 10.83 1.1863 7 3 1 48 85.19 3.13 1.1390 8 0 0 6 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.