D6.3 Th Zr2 Bartscher W, Rebizant J, Boeuf A, Caciuffo R, Rustichelli F, Fournier J, Kuhs W Journal of the Less-Common Metals 121 (1986) 455-460 Distribution of deuterium in the cubic Laves phases Th Zr2 Dx _cod_database_code 1008700 _database_code_amcsd 0016586 CELL PARAMETERS: 9.1540 9.1540 9.1540 90.000 90.000 90.000 SPACE GROUP: Fd3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 767.066 Density (g/cm3): 7.287 MAX. ABS. INTENSITY / VOLUME**2: 404.5285474 RIR: 18.076 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 16.78 9.74 5.2851 1 1 1 8 27.56 59.63 3.2364 2 2 0 12 32.44 100.00 2.7600 3 1 1 24 33.92 16.30 2.6425 2 2 2 8 43.07 2.83 2.1001 3 3 1 24 48.73 23.33 1.8686 4 2 2 24 51.90 8.12 1.7617 3 3 3 8 51.90 24.48 1.7617 5 1 1 24 56.90 23.74 1.6182 4 4 0 12 59.77 1.82 1.5473 5 3 1 48 64.37 8.98 1.4474 6 2 0 24 67.04 10.01 1.3960 5 3 3 24 67.92 5.37 1.3800 6 2 2 24 78.13 9.37 1.2233 6 4 2 48 80.61 5.45 1.1917 5 5 3 24 80.61 10.88 1.1917 7 3 1 48 84.71 3.15 1.1443 8 0 0 6 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.