N1.29 Ti3 Lengauer W Journal of the Less-Common Metals 125 (1986) 127-134 The crystal structure of $-eta-Ti3 N2-x: An additonal new phase in the Ti-N system _cod_database_code 1100032 _database_code_amcsd 0018228 CELL PARAMETERS: 2.9809 2.9809 21.6642 90.000 90.000 120.000 SPACE GROUP: R-3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 166.712 Density (g/cm3): 4.830 MAX. ABS. INTENSITY / VOLUME**2: 40.48083636 RIR: 2.729 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 35.00 24.40 2.5634 1 0 1 6 35.76 10.90 2.5112 0 1 2 6 37.36 43.42 2.4071 0 0 9 2 38.64 99.53 2.3304 1 0 4 6 40.68 100.00 2.2177 0 1 5 6 45.77 10.43 1.9824 1 0 7 6 48.73 20.87 1.8685 0 1 8 6 55.36 13.15 1.6595 1 0 10 6 58.99 4.12 1.5658 0 1 11 6 62.29 35.40 1.4905 1 1 0 6 66.82 17.04 1.4001 1 0 13 6 71.02 11.85 1.3273 0 1 14 6 73.50 2.08 1.2885 0 2 1 6 74.94 23.77 1.2672 1 1 9 12 75.76 9.39 1.2556 0 2 4 6 77.10 10.19 1.2370 2 0 5 6 79.66 4.83 1.2036 0 0 18 2 80.65 1.32 1.1913 0 2 7 6 82.85 3.00 1.1652 2 0 8 6 84.85 1.29 1.1427 0 1 17 6 88.09 2.52 1.1089 0 2 10 6 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.