As2 Cs2 Si Eisenmann B, Klein J Journal of the Less-Common Metals 175 (1991) 109-117 SiS2-isostrukturelle Anionen (SiP2^2-^),(GeAs2^2-^) und (SnAs2^2-^) in Alkaliverbindungen _cod_database_code 1008523 _database_code_amcsd 0016416 CELL PARAMETERS: 14.4250 7.5710 6.4200 90.000 90.000 90.000 SPACE GROUP: Ibam X-RAY WAVELENGTH: 1.541838 Cell Volume: 701.139 Density (g/cm3): 4.203 MAX. ABS. INTENSITY / VOLUME**2: 65.04327249 RIR: 5.039 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 12.27 1.89 7.2125 2 0 0 2 13.21 3.38 6.7038 1 1 0 4 21.90 28.37 4.0589 3 1 0 4 21.94 26.01 4.0512 2 1 1 8 23.50 13.08 3.7855 0 2 0 2 24.69 44.44 3.6063 4 0 0 2 26.59 1.39 3.3519 2 2 0 4 27.79 56.06 3.2100 0 0 2 2 28.05 100.00 3.1806 1 2 1 8 30.79 52.04 2.9037 4 1 1 8 30.89 1.34 2.8952 1 1 2 8 33.20 46.78 2.6988 3 2 1 8 34.35 11.93 2.6111 4 2 0 4 35.66 4.78 2.5178 3 1 2 8 36.13 1.08 2.4859 1 3 0 4 36.71 14.50 2.4483 0 2 2 4 37.51 38.62 2.3977 4 0 2 4 40.36 8.72 2.2346 3 3 0 4 41.81 14.86 2.1607 5 2 1 8 41.86 5.41 2.1581 6 1 1 8 43.85 4.06 2.0644 5 1 2 8 44.74 4.36 2.0256 4 2 2 8 45.62 4.11 1.9884 7 1 0 4 45.82 2.73 1.9802 2 1 3 8 47.89 3.36 1.8995 5 3 0 4 48.07 3.60 1.8928 0 4 0 2 49.32 16.95 1.8476 1 2 3 8 49.71 14.62 1.8340 3 3 2 8 50.68 11.85 1.8013 1 4 1 8 51.07 10.24 1.7883 4 1 3 8 52.53 1.04 1.7420 7 2 1 8 52.69 10.38 1.7371 3 2 3 8 53.99 6.08 1.6985 3 4 1 8 54.21 19.07 1.6920 8 1 1 8 54.27 8.38 1.6904 7 1 2 8 54.77 4.42 1.6759 4 4 0 4 56.28 1.48 1.6347 5 3 2 8 56.44 6.42 1.6304 0 4 2 4 57.41 7.14 1.6050 0 0 4 2 57.76 10.25 1.5962 7 3 0 4 58.90 1.05 1.5680 9 1 0 4 59.02 4.21 1.5650 5 2 3 8 59.06 1.52 1.5640 6 1 3 8 60.23 3.93 1.5366 5 4 1 8 62.20 2.03 1.4925 3 1 4 8 62.52 2.90 1.4856 4 4 2 8 62.89 1.12 1.4777 0 2 4 4 63.44 4.18 1.4663 4 0 4 4 65.28 9.08 1.4292 7 3 2 8 66.24 4.33 1.4110 1 4 3 8 68.64 2.13 1.3673 4 2 4 8 68.82 4.21 1.3642 4 5 1 8 69.07 2.41 1.3599 3 4 3 8 69.26 7.54 1.3566 8 1 3 8 72.51 1.93 1.3036 3 3 4 8 73.26 1.36 1.2921 11 1 0 4 74.58 1.70 1.2724 5 4 3 8 75.32 2.34 1.2618 0 6 0 2 76.24 1.19 1.2489 7 1 4 8 76.39 2.16 1.2468 9 3 2 8 77.93 1.19 1.2260 5 3 4 8 78.07 1.17 1.2241 0 4 4 4 79.03 2.88 1.2117 1 2 5 8 80.39 1.88 1.1945 4 1 5 8 80.67 1.53 1.1910 4 6 0 4 81.68 2.04 1.1788 3 2 5 8 82.06 2.49 1.1744 0 6 2 4 82.49 2.15 1.1693 4 5 3 8 82.65 3.04 1.1674 12 1 1 8 82.98 1.76 1.1636 11 3 0 4 83.37 1.86 1.1592 4 4 4 8 85.00 4.39 1.1411 8 5 1 8 85.87 4.69 1.1318 7 3 4 8 87.32 3.52 1.1166 4 6 2 8 89.61 3.99 1.0940 11 3 2 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.