As2 Cs2 Sn Eisenmann B, Klein J Journal of the Less-Common Metals 175 (1991) 109-117 SiS2-isostrukturelle Anionen (SiP2^2-^),(GeAs2^2-^) und (SnAs2^2-^) in Alkaliverbindungen _cod_database_code 1008524 _database_code_amcsd 0016417 CELL PARAMETERS: 14.6570 7.7330 6.9530 90.000 90.000 90.000 SPACE GROUP: Ibam X-RAY WAVELENGTH: 1.541838 Cell Volume: 788.071 Density (g/cm3): 4.503 MAX. ABS. INTENSITY / VOLUME**2: 55.23875670 RIR: 3.994 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 12.08 26.71 7.3285 2 0 0 2 12.94 40.40 6.8395 1 1 0 4 21.03 17.54 4.2247 2 1 1 8 21.51 72.15 4.1304 3 1 0 4 23.00 3.76 3.8665 0 2 0 2 24.29 24.24 3.6642 4 0 0 2 25.62 37.10 3.4765 0 0 2 2 26.06 12.12 3.4197 2 2 0 4 27.08 100.00 3.2928 1 2 1 8 28.42 12.85 3.1410 2 0 2 4 28.81 26.95 3.0991 1 1 2 8 29.89 45.67 2.9896 4 1 1 8 32.21 38.30 2.7792 3 2 1 8 32.67 1.78 2.7411 5 1 0 4 33.70 32.67 2.6596 4 2 0 4 34.70 37.98 2.5852 0 2 2 4 35.36 7.65 2.5387 1 3 0 4 35.60 71.70 2.5220 4 0 2 4 36.79 4.86 2.4428 6 0 0 2 36.87 9.29 2.4379 2 2 2 8 39.25 1.39 2.2953 2 3 1 8 39.53 1.09 2.2798 3 3 0 4 40.75 21.24 2.2143 5 2 1 8 40.86 2.07 2.2087 6 1 1 8 41.97 13.38 2.1525 5 1 2 8 42.55 1.99 2.1247 2 1 3 8 43.84 2.63 2.0652 6 2 0 4 44.17 3.46 2.0502 1 3 2 8 46.08 18.69 1.9699 1 2 3 8 46.94 9.04 1.9357 5 3 0 4 47.70 25.20 1.9064 3 3 2 8 47.91 9.92 1.8988 4 1 3 8 48.71 2.79 1.8693 2 4 0 4 49.32 13.03 1.8477 1 4 1 8 49.50 9.31 1.8413 3 2 3 8 49.77 4.06 1.8321 8 0 0 2 51.33 1.15 1.7799 7 2 1 8 51.47 3.13 1.7755 6 2 2 8 52.36 14.83 1.7473 7 1 2 8 52.58 8.14 1.7404 3 4 1 8 52.66 12.68 1.7383 0 0 4 2 53.03 18.32 1.7269 8 1 1 8 53.60 7.54 1.7099 4 4 0 4 54.23 1.01 1.6913 2 0 4 4 54.29 8.93 1.6896 0 4 2 4 54.46 1.79 1.6847 1 1 4 8 55.84 1.48 1.6464 2 4 2 8 55.88 6.59 1.6453 5 2 3 8 56.63 12.46 1.6252 7 3 0 4 57.52 6.86 1.6022 3 1 4 8 57.86 3.64 1.5936 9 1 0 4 58.73 3.82 1.5721 5 4 1 8 58.80 2.44 1.5705 4 0 4 4 59.67 1.79 1.5496 2 2 4 8 60.16 1.64 1.5381 1 5 0 4 62.09 3.68 1.4948 8 2 2 8 62.85 1.23 1.4787 2 5 1 8 62.93 5.08 1.4770 1 4 3 8 63.05 1.29 1.4745 3 5 0 4 63.15 2.50 1.4723 7 3 2 8 63.40 1.08 1.4671 9 2 1 8 63.99 7.17 1.4550 4 2 4 8 65.03 1.73 1.4343 1 3 4 8 65.74 3.43 1.4204 3 4 3 8 65.96 1.16 1.4163 6 0 4 4 66.13 7.68 1.4131 8 1 3 8 67.05 2.59 1.3959 4 5 1 8 67.39 2.84 1.3896 6 4 2 8 69.61 1.35 1.3506 10 0 2 4 70.86 1.04 1.3299 6 2 4 8 71.19 1.72 1.3244 5 4 3 8 71.90 2.26 1.3131 11 1 0 4 72.53 3.18 1.3034 1 2 5 8 73.18 3.59 1.2933 5 3 4 8 73.48 3.28 1.2888 0 6 0 2 73.92 1.82 1.2821 4 1 5 8 74.06 6.06 1.2801 9 3 2 8 74.55 1.17 1.2729 2 4 4 8 74.55 2.63 1.2729 5 5 2 8 75.17 1.83 1.2640 3 2 5 8 75.37 1.68 1.2610 8 0 4 4 76.73 1.87 1.2421 8 4 2 8 78.46 3.48 1.2190 4 4 4 8 78.86 1.35 1.2138 4 5 3 8 79.28 1.12 1.2085 0 6 2 4 80.36 1.48 1.1949 5 2 5 8 80.86 3.64 1.1887 12 1 1 8 80.99 6.16 1.1872 7 3 4 8 82.04 1.96 1.1747 9 1 4 8 82.32 2.00 1.1713 7 5 2 8 82.86 3.03 1.1651 8 5 1 8 84.02 1.00 1.1519 1 5 4 8 84.40 5.88 1.1477 4 6 2 8 86.46 1.44 1.1256 1 4 5 8 86.95 5.26 1.1205 11 3 2 8 87.97 1.38 1.1100 0 2 6 4 88.49 2.64 1.1049 4 0 6 4 89.00 1.08 1.0999 3 4 5 8 89.35 2.39 1.0965 8 1 5 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.