Cuproiridsite Furubayashi T, Matsumoto T, Hagino T, Nagata S Journal of the Physical Society of Japan 63 (1994) 3333-3339 Structural and magnetic studies of metal-insulator transition in thiospinel CuIr2S4 Sample: T = 10 K, low temperature form _database_code_amcsd 0014172 CELL PARAMETERS: 6.8645 6.8645 10.0257 90.000 90.000 90.000 SPACE GROUP: I4_1/amd X-RAY WAVELENGTH: 1.541838 Cell Volume: 472.425 Density (g/cm3): 8.101 MAX. ABS. INTENSITY / VOLUME**2: 214.6970565 RIR: 8.630 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 15.65 98.31 5.6641 1 0 1 8 25.54 6.98 3.4871 1 1 2 8 25.96 3.23 3.4323 2 0 0 4 29.73 45.99 3.0047 1 0 3 8 30.45 100.00 2.9354 2 1 1 16 31.59 48.80 2.8320 2 0 2 8 35.83 26.03 2.5064 0 0 4 2 37.04 49.33 2.4270 2 2 0 4 39.87 11.70 2.2608 2 1 3 16 40.43 7.20 2.2308 3 0 1 8 44.77 1.35 2.0242 2 0 4 8 45.54 2.46 1.9920 3 1 2 16 47.22 18.86 1.9247 1 0 5 8 48.20 10.26 1.8880 3 0 3 8 48.68 30.96 1.8704 3 2 1 16 52.48 57.78 1.7435 2 2 4 8 53.39 28.19 1.7161 4 0 0 4 54.67 9.30 1.6788 2 1 5 16 55.55 6.04 1.6543 3 2 3 16 55.99 7.24 1.6424 4 1 1 16 61.49 7.33 1.5080 3 0 5 8 61.75 9.06 1.5024 2 0 6 8 62.31 10.97 1.4902 4 1 3 16 63.37 14.92 1.4677 4 2 2 16 65.97 16.49 1.4160 4 0 4 8 66.71 1.08 1.4021 1 0 7 8 67.89 5.78 1.3807 3 2 5 16 69.05 2.40 1.3602 5 0 1 8 69.05 3.05 1.3602 4 3 1 16 72.88 5.11 1.2979 2 1 7 16 74.01 9.23 1.2809 4 1 5 16 74.75 3.59 1.2699 5 0 3 8 74.75 5.34 1.2699 4 3 3 16 75.13 5.99 1.2645 5 2 1 16 75.93 4.19 1.2532 0 0 8 2 78.88 8.46 1.2135 4 4 0 4 80.67 1.22 1.1910 5 2 3 16 84.69 3.88 1.1445 3 2 7 16 85.77 3.53 1.1328 5 0 5 8 85.77 5.53 1.1328 4 3 5 16 86.00 7.23 1.1304 4 2 6 16 86.86 4.76 1.1214 6 1 1 16 87.44 3.12 1.1154 6 0 2 8 87.63 6.89 1.1135 2 2 8 8 89.03 1.61 1.0996 1 0 9 8 89.79 7.35 1.0922 4 4 4 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.