Ba Ca Fe4 O8 Herrmann D, Bacmann M Materials Research Bulletin 6 (1971) 725-736 Structure nucleaire de Ba Ca Fe4 O8 _cod_database_code 1008057 _database_code_amcsd 0015999 CELL PARAMETERS: 5.4070 5.4070 7.7030 90.000 90.000 120.000 SPACE GROUP: P-31m X-RAY WAVELENGTH: 1.541838 Cell Volume: 195.031 Density (g/cm3): 4.502 MAX. ABS. INTENSITY / VOLUME**2: 75.05008953 RIR: 5.429 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 11.49 23.98 7.7030 0 0 1 2 18.95 2.78 4.6826 1 0 0 6 22.22 9.77 4.0013 1 0 1 12 23.09 5.31 3.8515 0 0 2 2 30.04 100.00 2.9746 1 0 2 12 33.14 79.96 2.7035 1 1 0 6 34.94 3.32 2.5677 0 0 3 2 35.18 24.97 2.5510 2 -1 1 6 35.18 2.67 2.5510 1 1 1 6 40.05 6.22 2.2514 1 0 3 12 40.26 2.23 2.2401 2 0 1 12 45.33 29.60 2.0006 2 0 2 12 47.20 10.78 1.9258 0 0 4 2 52.92 2.45 1.7301 2 0 3 12 53.09 1.03 1.7249 3 -1 1 12 57.29 12.91 1.6082 3 -1 2 12 57.29 13.28 1.6082 2 1 2 12 58.88 19.15 1.5685 2 -1 4 6 58.88 9.58 1.5685 1 1 4 6 59.20 21.01 1.5609 3 0 0 6 60.52 1.67 1.5298 3 0 1 12 63.88 1.31 1.4572 3 -1 3 12 63.88 1.37 1.4572 2 1 3 12 64.41 1.17 1.4466 3 0 2 12 69.54 6.77 1.3518 2 2 0 6 70.33 3.08 1.3385 1 1 5 6 70.33 2.28 1.3385 2 -1 5 6 70.62 1.27 1.3338 3 0 3 12 70.76 1.85 1.3314 2 2 1 6 77.02 4.10 1.2381 1 0 6 12 77.58 4.41 1.2306 4 -1 2 12 77.58 4.30 1.2306 3 1 2 12 78.95 10.02 1.2126 3 0 4 12 86.45 2.81 1.1257 2 0 6 12 86.99 3.02 1.1201 4 0 2 12 88.34 2.46 1.1064 4 -2 4 6 88.34 4.46 1.1064 2 2 4 6 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.