La3 O11 Ru3 Abraham F, Trehoux J, Thomas D Materials Research Bulletin 13 (1978) 805-810 La liaison metal-metal dans les clusters M12 O36: II-Preparation et etude structurelle de la phase La3 Ru3 O11 _cod_database_code 1004063 _database_code_amcsd 0014268 CELL PARAMETERS: 9.4660 9.4660 9.4660 90.000 90.000 90.000 SPACE GROUP: Pn3 X-RAY WAVELENGTH: 1.541838 Cell Volume: 848.202 Density (g/cm3): 7.015 MAX. ABS. INTENSITY / VOLUME**2: 145.8578639 RIR: 6.770 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 23.01 2.11 3.8645 2 1 1 24 26.64 16.17 3.3467 2 2 0 12 28.28 41.31 3.1553 2 2 1 24 29.85 97.24 2.9934 3 0 1 12 29.85 2.76 2.9934 3 1 0 12 31.34 42.24 2.8541 3 1 1 24 32.77 14.67 2.7326 2 2 2 8 35.48 24.87 2.5299 3 1 2 24 35.48 7.57 2.5299 3 2 1 24 39.24 6.51 2.2958 3 2 2 24 40.43 10.57 2.2312 3 3 0 12 40.43 4.23 2.2312 4 1 1 24 41.59 3.91 2.1716 3 3 1 24 42.72 1.77 2.1167 4 0 2 12 42.72 5.38 2.1167 4 2 0 12 43.83 1.76 2.0657 4 2 1 24 43.83 1.82 2.0657 4 1 2 24 49.07 8.27 1.8564 5 0 1 12 49.07 3.29 1.8564 5 1 0 12 49.07 36.28 1.8564 4 3 1 24 50.07 17.16 1.8217 5 1 1 24 50.07 1.76 1.8217 3 3 3 8 52.98 2.16 1.7282 5 1 2 24 54.86 9.96 1.6734 4 4 0 12 55.79 8.77 1.6478 5 2 2 24 56.70 1.79 1.6234 5 0 3 12 56.70 1.20 1.6234 5 3 0 12 56.70 1.06 1.6234 4 3 3 24 58.50 4.54 1.5777 6 0 0 6 58.50 19.92 1.5777 4 4 2 24 60.27 1.40 1.5356 5 3 2 24 60.27 3.25 1.5356 5 2 3 24 62.01 3.53 1.4967 6 0 2 12 62.01 4.86 1.4967 6 2 0 12 62.86 2.99 1.4783 6 2 1 24 62.86 3.11 1.4783 6 1 2 24 63.71 1.43 1.4606 5 4 1 24 63.71 3.29 1.4606 5 1 4 24 64.56 3.70 1.4436 5 3 3 24 65.40 1.48 1.4271 6 2 2 24 67.06 7.93 1.3957 6 1 3 24 68.70 3.95 1.3663 4 4 4 8 70.32 1.28 1.3387 5 4 3 24 70.32 2.60 1.3387 5 3 4 24 75.10 1.35 1.2649 6 2 4 24 76.67 5.94 1.2429 7 3 0 12 77.45 1.09 1.2324 7 3 1 24 77.45 3.22 1.2324 5 5 3 24 77.45 1.07 1.2324 7 1 3 24 79.77 1.32 1.2022 6 1 5 24 79.77 2.30 1.2022 7 2 3 24 81.31 4.01 1.1832 8 0 0 6 82.08 1.91 1.1741 6 5 2 24 82.08 1.98 1.1741 6 2 5 24 82.85 1.02 1.1652 7 1 4 24 85.90 1.37 1.1314 6 5 3 24 87.43 5.24 1.1156 6 6 0 12 88.95 6.80 1.1004 7 4 3 24 88.95 1.53 1.1004 7 5 0 12 88.95 2.54 1.1004 8 1 3 24 89.71 1.05 1.0930 7 5 1 24 89.71 1.25 1.0930 5 5 5 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.