O5 Ta Ti Tl Rebbah A, Desgardin G, Raveau B Materials Research Bulletin 14 (1979) 1125-1131 Les oxydes A Ti M O5: echangeures cationiques _cod_database_code 1001280 _database_code_amcsd 0014273 CELL PARAMETERS: 6.4440 3.8010 18.8600 90.000 90.000 90.000 SPACE GROUP: Pnma X-RAY WAVELENGTH: 1.541838 Cell Volume: 461.950 Density (g/cm3): 7.378 MAX. ABS. INTENSITY / VOLUME**2: 152.9776282 RIR: 6.751 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 9.38 3.67 9.4300 0 0 2 2 14.53 1.25 6.0979 1 0 1 4 19.73 6.39 4.4999 1 0 3 4 23.38 41.21 3.8052 1 0 4 4 23.88 3.14 3.7261 0 1 1 4 27.42 68.40 3.2527 0 1 3 4 27.65 14.22 3.2257 1 1 1 8 27.69 61.98 3.2220 2 0 0 2 29.29 3.68 3.0489 2 0 2 4 30.79 100.00 2.9037 1 1 3 8 31.19 2.59 2.8673 2 0 3 4 31.67 70.75 2.8251 1 0 6 4 36.13 1.70 2.4858 1 0 7 4 36.34 3.50 2.4725 1 1 5 8 36.56 5.71 2.4578 2 1 0 4 36.88 6.95 2.4372 2 1 1 8 39.36 30.53 2.2891 2 1 3 8 40.75 1.39 2.2140 1 0 8 4 41.06 9.54 2.1981 0 1 7 4 43.50 8.44 2.0804 1 1 7 8 44.58 6.65 2.0326 3 0 3 4 46.46 10.00 1.9547 3 0 4 4 47.86 20.18 1.9005 0 2 0 2 48.25 8.83 1.8860 0 0 10 2 48.95 5.66 1.8609 3 1 1 8 49.68 9.31 1.8351 0 1 9 4 50.25 9.09 1.8158 2 1 7 8 50.95 16.20 1.7924 3 1 3 8 51.53 13.05 1.7735 3 0 6 4 51.80 13.73 1.7650 1 1 9 8 52.06 1.35 1.7567 2 0 9 4 53.93 8.08 1.7002 1 2 4 8 56.19 14.99 1.6369 2 2 0 4 56.54 8.51 1.6277 2 0 10 4 57.11 1.15 1.6128 2 2 2 8 57.18 4.36 1.6110 4 0 0 2 57.33 5.51 1.6071 3 1 6 8 57.82 9.98 1.5946 2 1 9 8 58.09 1.11 1.5880 4 0 2 4 58.53 21.88 1.5769 1 2 6 8 58.75 2.75 1.5717 0 0 12 2 59.21 1.85 1.5606 4 0 3 4 60.24 3.02 1.5363 3 1 7 8 61.00 2.95 1.5189 1 1 11 8 62.63 3.75 1.4833 4 1 0 4 62.85 1.02 1.4787 4 1 1 8 64.55 5.50 1.4436 4 1 3 8 66.15 3.02 1.4126 2 0 12 4 67.08 4.02 1.3953 3 1 9 8 67.47 3.06 1.3882 3 2 3 8 68.91 5.23 1.3626 3 2 4 8 69.33 2.12 1.3554 0 1 13 4 70.32 4.81 1.3387 0 2 10 4 71.07 5.38 1.3264 1 1 13 8 71.21 1.32 1.3241 2 1 12 8 72.78 4.75 1.2994 4 1 7 8 72.96 8.00 1.2966 3 2 6 8 75.27 1.34 1.2625 5 0 3 4 76.20 2.82 1.2494 2 1 13 8 76.65 1.80 1.2432 5 0 4 4 76.73 2.74 1.2420 0 3 3 4 77.16 5.94 1.2362 2 2 10 8 77.71 3.07 1.2289 4 2 0 4 78.00 2.41 1.2249 4 0 10 4 78.41 5.24 1.2196 1 3 3 8 78.53 1.23 1.2180 5 1 1 8 79.06 2.05 1.2112 0 2 12 4 79.10 2.00 1.2107 4 1 9 8 79.46 1.34 1.2061 4 2 3 8 80.09 1.61 1.1982 5 1 3 8 80.56 1.57 1.1925 5 0 6 4 82.11 2.17 1.1737 1 1 15 8 83.34 2.63 1.1595 1 0 16 4 83.40 2.89 1.1589 2 3 3 8 84.53 3.35 1.1463 3 1 13 8 85.31 2.49 1.1378 5 1 6 8 85.69 2.69 1.1337 2 2 12 8 86.15 1.06 1.1288 1 3 7 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.