Li1.6 O8 Sn2.1 Ti0.7 Zn1.6 Choisnet J, Raveau B Materials Research Bulletin 14 (1979) 1381-1389 Une nouvelle structure hexagonale compacte ordonne: les oxydes (Sn - x3)octa (M - Li)tetra O8 avec X = Sn(Ti)+ M + Li et M = Zn, Mg _cod_database_code 1001290 _database_code_amcsd 0014278 CELL PARAMETERS: 6.0110 6.0110 9.8150 90.000 90.000 120.000 SPACE GROUP: P6_3mc X-RAY WAVELENGTH: 1.541838 Cell Volume: 307.124 Density (g/cm3): 5.693 MAX. ABS. INTENSITY / VOLUME**2: 59.49528288 RIR: 3.403 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 17.03 17.38 5.2057 1 0 0 6 18.08 7.59 4.9075 0 0 2 1 19.30 31.91 4.5989 1 0 1 6 24.94 62.92 3.5709 1 0 2 6 29.73 24.33 3.0055 1 1 0 6 32.32 63.48 2.7700 1 0 3 6 34.46 26.45 2.6028 2 0 0 6 35.01 100.00 2.5630 1 1 2 6 35.69 51.04 2.5159 2 0 1 6 36.62 12.49 2.4537 0 0 4 1 39.18 11.11 2.2994 2 0 2 6 44.48 15.67 2.0369 2 0 3 6 46.13 2.05 1.9676 2 1 0 12 47.11 1.23 1.9292 2 1 1 12 49.63 6.87 1.8368 1 0 5 6 49.94 18.26 1.8262 2 1 2 12 51.16 19.54 1.7854 2 0 4 6 52.75 3.76 1.7352 3 0 0 6 54.41 32.25 1.6861 2 1 3 12 56.23 22.31 1.6360 3 0 2 6 56.23 2.05 1.6358 0 0 6 1 58.93 47.08 1.5673 2 0 5 6 61.73 35.60 1.5028 2 2 0 6 64.90 2.87 1.4368 1 1 6 6 65.33 1.37 1.4284 3 1 1 12 67.39 6.04 1.3897 2 1 5 12 67.64 5.38 1.3851 3 1 2 12 69.42 9.60 1.3539 1 0 7 6 71.41 10.35 1.3209 3 1 3 12 72.65 2.82 1.3014 4 0 0 6 73.39 5.61 1.2901 4 0 1 6 73.96 9.66 1.2815 2 2 4 6 77.86 1.17 1.2269 0 0 8 1 79.21 1.81 1.2093 4 0 3 6 80.73 1.36 1.1903 3 0 6 6 83.03 2.49 1.1631 3 1 5 12 84.22 2.96 1.1497 4 0 4 6 84.93 7.86 1.1419 2 1 7 12 85.48 2.17 1.1359 1 1 8 6 86.81 1.64 1.1219 3 2 3 12 88.31 3.35 1.1067 4 1 2 12 88.31 2.53 1.1067 2 2 6 6 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.