Clinobisvanite Sleight A W, Chen H-Y, Ferretti A, Cox D E Materials Research Bulletin 14 (1979) 1571-1581 Crystal growth and structure of BiVO4 Locality: synthetic Sample: T = 295 K _database_code_amcsd 0014280 CELL PARAMETERS: 5.1935 5.0898 11.6972 90.000 90.000 90.387 SPACE GROUP: I2/b X-RAY WAVELENGTH: 1.541838 Cell Volume: 309.195 Density (g/cm3): 6.957 MAX. ABS. INTENSITY / VOLUME**2: 168.2537603 RIR: 7.874 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 15.15 2.54 5.8486 0 0 2 2 18.69 34.84 4.7466 1 0 1 4 19.02 45.48 4.6670 0 1 1 4 28.63 18.40 3.1181 1 0 3 4 28.84 6.24 3.0952 0 1 3 4 28.85 93.76 3.0949 1 -1 2 4 28.99 94.42 3.0798 1 1 2 4 30.57 31.30 2.9243 0 0 4 2 34.54 20.64 2.5967 2 0 0 2 35.27 20.68 2.5448 0 2 0 2 37.91 1.29 2.3733 2 0 2 4 39.50 5.15 2.2815 1 -1 4 4 39.61 5.22 2.2751 2 -1 1 4 39.83 13.35 2.2632 2 1 1 4 40.10 11.02 2.2486 -1 2 1 4 40.32 3.38 2.2371 1 2 1 4 42.38 3.98 2.1330 1 0 5 4 42.53 12.17 2.1256 0 1 5 4 45.50 6.46 1.9934 2 -1 3 4 45.70 2.65 1.9853 2 1 3 4 45.94 6.04 1.9755 -1 2 3 4 46.13 9.27 1.9677 1 2 3 4 46.79 25.84 1.9417 2 0 4 4 47.35 25.41 1.9197 0 2 4 4 50.01 10.20 1.8237 -2 2 0 2 50.38 10.97 1.8114 2 2 0 2 53.28 14.50 1.7193 1 -1 6 4 53.37 15.12 1.7168 1 1 6 4 53.51 3.18 1.7125 3 0 1 4 54.67 3.21 1.6790 0 3 1 4 55.81 3.26 1.6471 2 -1 5 4 55.98 2.83 1.6426 2 1 5 4 57.98 4.95 1.5907 1 0 7 4 58.32 3.72 1.5822 3 0 3 4 58.36 13.45 1.5812 3 -1 2 4 58.61 10.33 1.5751 3 1 2 4 59.27 1.21 1.5590 2 0 6 4 59.33 9.76 1.5576 -1 3 2 4 59.41 2.00 1.5557 0 3 3 4 59.58 13.10 1.5518 1 3 2 4 59.76 10.68 1.5474 2 -2 4 4 60.08 10.14 1.5399 2 2 4 4 63.64 2.90 1.4621 0 0 8 2 65.95 1.76 1.4164 3 2 1 4 66.06 2.22 1.4143 -2 3 1 4 68.29 1.60 1.3734 0 3 5 4 69.30 1.65 1.3559 1 1 8 4 69.64 1.41 1.3501 -1 2 7 4 69.79 2.28 1.3476 1 2 7 4 69.80 1.66 1.3474 3 -2 3 4 72.85 3.05 1.2983 4 0 0 2 74.47 5.65 1.2741 2 0 8 4 74.58 2.78 1.2724 0 4 0 2 74.90 5.18 1.2678 0 2 8 4 75.50 1.76 1.2593 0 1 9 4 75.73 4.04 1.2560 3 -1 6 4 75.94 5.85 1.2530 3 1 6 4 75.95 1.15 1.2528 4 -1 1 4 76.58 5.89 1.2441 -1 3 6 4 76.80 3.55 1.2412 1 3 6 4 78.63 1.56 1.2168 -2 3 5 4 79.05 1.84 1.2113 2 3 5 4 79.76 1.06 1.2023 3 0 7 4 80.73 4.53 1.1904 3 -3 2 4 81.03 4.31 1.1866 4 0 4 4 81.36 4.18 1.1827 3 3 2 4 82.71 3.85 1.1668 0 4 4 4 83.33 2.41 1.1597 -4 2 0 2 83.89 2.15 1.1534 4 2 0 2 84.58 2.26 1.1457 -2 4 0 2 85.03 3.26 1.1408 2 -2 8 4 85.14 2.09 1.1396 2 4 0 2 85.31 3.06 1.1377 2 2 8 4 85.68 1.66 1.1338 2 -1 9 4 85.82 1.13 1.1323 2 1 9 4 87.60 2.99 1.1138 1 -1 10 4 87.67 2.56 1.1131 1 1 10 4 88.04 1.24 1.1094 4 -1 5 4 88.32 1.19 1.1066 4 1 5 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.