Sinoite Billy M, Labbe J, Selvaraj A, Roult G Materials Research Bulletin 15 (1980) 1207-1213 Modifications structurales de l'oxynitrure de silicium sous contraintes thermiques _cod_database_code 1001781 _database_code_amcsd 0014289 CELL PARAMETERS: 8.8840 5.5220 4.8730 90.000 90.000 90.000 SPACE GROUP: Cmc2_1 X-RAY WAVELENGTH: 1.541838 Cell Volume: 239.057 Density (g/cm3): 2.783 MAX. ABS. INTENSITY / VOLUME**2: 13.17200133 RIR: 1.541 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.92 54.90 4.6899 1 1 0 4 19.99 100.00 4.4420 2 0 0 2 26.38 90.89 3.3791 1 1 1 4 32.43 11.55 2.7610 0 2 0 2 34.36 28.72 2.6097 3 1 0 4 36.89 42.05 2.4365 0 0 2 1 37.44 38.38 2.4022 0 2 1 2 39.16 18.19 2.3006 3 1 1 4 40.62 3.75 2.2210 4 0 0 2 41.78 7.07 2.1621 1 1 2 4 42.31 5.67 2.1362 2 0 2 2 42.80 11.91 2.1130 2 2 1 4 49.92 4.86 1.8269 0 2 2 2 50.65 7.99 1.8024 1 3 0 4 51.30 8.72 1.7810 3 1 2 4 54.23 9.55 1.6914 5 1 0 4 56.03 2.14 1.6414 4 0 2 2 56.42 2.14 1.6308 4 2 1 4 57.69 14.40 1.5979 5 1 1 4 59.09 9.26 1.5633 3 3 0 4 60.30 6.78 1.5349 1 1 3 4 62.38 2.79 1.4886 3 3 1 4 62.75 4.12 1.4807 6 0 0 2 64.29 5.30 1.4490 1 3 2 4 66.82 14.83 1.4000 0 2 3 2 67.40 4.52 1.3894 5 1 2 4 67.90 4.52 1.3805 0 4 0 2 67.98 9.23 1.3790 3 1 3 4 70.53 9.94 1.3353 2 2 3 4 70.96 3.58 1.3282 0 4 1 2 71.58 5.60 1.3183 2 4 0 4 71.74 7.08 1.3157 3 3 2 4 72.43 1.08 1.3049 6 2 0 4 74.18 7.38 1.2784 5 3 0 4 75.07 6.26 1.2653 6 0 2 2 75.41 11.32 1.2605 6 2 1 4 78.52 1.57 1.2183 0 0 4 1 79.86 2.49 1.2011 0 4 2 2 82.30 8.01 1.1716 5 1 3 4 83.35 3.14 1.1595 2 4 2 4 84.16 1.25 1.1503 6 2 2 4 85.85 6.06 1.1320 5 3 2 4 86.38 1.95 1.1264 3 3 3 4 87.93 1.03 1.1105 8 0 0 2 88.59 1.44 1.1039 3 1 4 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.