Mn6 Ni16 P7 Chaudouet P, Madar R, Fruchart R Materials Research Bulletin 18 (1983) 713-719 Etude de nouveaux pnictures ternaires de metaux de transition isostructuraux des phases G, Ni16 Mn6 P7, Ni16 Mn6 As7 _cod_database_code 1008203 _database_code_amcsd 0016139 CELL PARAMETERS: 11.0310 11.0310 11.0310 90.000 90.000 90.000 SPACE GROUP: Fm3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 1342.285 Density (g/cm3): 7.350 MAX. ABS. INTENSITY / VOLUME**2: 104.3251749 RIR: 4.622 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 13.91 5.77 6.3688 1 1 1 8 16.07 9.47 5.5155 2 0 0 6 28.02 3.18 3.1844 2 2 2 8 32.47 14.08 2.7578 4 0 0 6 35.47 1.64 2.5307 3 3 1 24 36.43 5.57 2.4666 4 2 0 24 40.04 17.73 2.2517 4 2 2 24 42.59 48.14 2.1229 5 1 1 24 42.59 39.68 2.1229 3 3 3 8 46.57 100.00 1.9500 4 4 0 12 48.84 26.87 1.8646 5 3 1 48 49.58 14.90 1.8385 6 0 0 6 49.58 1.20 1.8385 4 4 2 24 52.46 6.50 1.7442 6 2 0 24 54.55 9.85 1.6822 5 3 3 24 55.24 3.92 1.6630 6 2 2 24 57.92 2.20 1.5922 4 4 4 8 63.07 1.11 1.4741 6 4 2 48 64.93 2.61 1.4361 5 5 3 24 64.93 4.76 1.4361 7 3 1 48 67.99 4.78 1.3789 8 0 0 6 72.74 4.65 1.3000 8 2 2 24 72.74 9.39 1.3000 6 6 0 12 74.49 4.47 1.2738 7 5 1 48 74.49 4.82 1.2738 5 5 5 8 79.09 3.04 1.2108 9 1 1 24 79.09 7.74 1.2108 7 5 3 48 79.66 4.28 1.2036 8 4 2 48 81.93 1.39 1.1759 6 6 4 24 83.62 8.50 1.1564 9 3 1 48 86.43 8.77 1.1258 8 4 4 24 88.11 16.41 1.1087 9 3 3 24 88.67 2.00 1.1031 8 6 0 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.