Nierite Billy M, Labbe J, Selvaraj A, Roult G Materials Research Bulletin 18 (1983) 921-934 Modifications structurales du nitrure de silicium en fonction de la temperature _cod_database_code 1001241 _database_code_amcsd 0014304 CELL PARAMETERS: 7.7809 7.7809 5.6407 90.000 90.000 120.000 SPACE GROUP: P31c X-RAY WAVELENGTH: 1.541838 Cell Volume: 295.749 Density (g/cm3): 3.150 MAX. ABS. INTENSITY / VOLUME**2: 8.470114327 RIR: 0.876 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 13.14 20.61 6.7385 1 0 0 6 20.53 100.00 4.3253 1 0 1 6 22.86 43.91 3.8905 1 1 0 3 26.45 31.48 3.3692 2 0 0 6 30.91 86.25 2.8925 2 0 1 6 31.73 7.69 2.8203 0 0 2 1 34.47 84.14 2.6017 1 0 2 6 35.24 88.36 2.5469 2 1 0 6 38.79 14.06 2.3212 3 -1 1 6 38.79 31.37 2.3212 2 1 1 6 39.46 7.44 2.2834 1 1 2 3 39.46 1.45 2.2834 2 -1 2 3 40.15 3.73 2.2462 3 0 0 6 41.77 32.67 2.1627 2 0 2 6 43.36 42.89 2.0868 3 0 1 6 46.70 3.31 1.9452 2 2 0 3 48.14 1.23 1.8902 3 -1 2 6 48.14 6.89 1.8902 2 1 2 6 48.72 6.43 1.8689 3 1 0 6 50.39 10.46 1.8111 1 0 3 6 51.51 16.70 1.7741 4 -1 1 6 56.01 6.40 1.6419 2 0 3 6 57.06 1.11 1.6142 4 0 1 6 57.56 17.78 1.6013 4 -2 2 3 57.56 4.85 1.6013 2 2 2 3 59.32 2.31 1.5579 4 -1 2 6 59.32 1.40 1.5579 3 1 2 6 59.83 1.44 1.5459 3 2 0 6 61.28 1.58 1.5127 2 1 3 6 61.28 5.83 1.5127 3 -1 3 6 62.27 1.52 1.4909 5 -2 1 6 62.27 31.93 1.4909 3 2 1 6 64.65 24.27 1.4418 3 0 3 6 65.61 19.90 1.4229 5 -1 1 6 65.61 1.37 1.4229 4 1 1 6 66.28 14.81 1.4102 0 0 4 1 67.91 3.50 1.3803 1 0 4 6 69.32 15.15 1.3556 5 -2 2 6 69.32 17.84 1.3556 3 2 2 6 69.78 1.26 1.3477 5 0 0 6 71.11 3.90 1.3258 2 -1 4 3 71.13 4.13 1.3255 3 1 3 6 71.13 1.92 1.3255 4 -1 3 6 72.05 6.51 1.3108 5 0 1 6 72.49 13.16 1.3039 4 1 2 6 72.49 5.84 1.3039 5 -1 2 6 72.69 3.08 1.3008 2 0 4 6 72.95 12.43 1.2968 3 3 0 3 74.51 1.89 1.2734 4 2 0 6 76.72 7.09 1.2422 6 -2 1 6 76.72 1.13 1.2422 4 2 1 6 77.35 8.30 1.2337 3 -1 4 6 77.35 3.54 1.2337 2 1 4 6 78.69 3.42 1.2160 5 0 2 6 79.13 1.73 1.2103 5 1 0 6 80.42 10.72 1.1941 5 -2 3 6 80.42 1.33 1.1941 3 2 3 6 81.31 5.42 1.1833 5 1 1 6 81.73 1.37 1.1782 6 -3 2 3 83.25 2.64 1.1606 6 -2 2 6 83.45 7.90 1.1583 4 1 3 6 86.45 1.45 1.1257 3 1 4 6 87.76 1.08 1.1122 6 -1 2 6 87.76 3.49 1.1122 5 1 2 6 88.84 1.17 1.1015 6 0 1 6 89.46 2.03 1.0954 5 0 3 6 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.