Nierite Billy M, Labbe J, Selvaraj A, Roult G Materials Research Bulletin 18 (1983) 921-934 Modifications structurales du nitrure de silicium en fonction de la temperature _cod_database_code 1001243 _database_code_amcsd 0014306 CELL PARAMETERS: 7.7910 7.7910 5.6492 90.000 90.000 120.000 SPACE GROUP: P31c X-RAY WAVELENGTH: 1.541838 Cell Volume: 296.964 Density (g/cm3): 3.137 MAX. ABS. INTENSITY / VOLUME**2: 7.923438091 RIR: 0.822 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 13.12 43.68 6.7472 1 0 0 6 20.50 98.48 4.3314 1 0 1 6 22.83 29.20 3.8955 1 1 0 3 26.42 39.30 3.3736 2 0 0 6 30.87 83.33 2.8964 2 0 1 6 31.68 4.90 2.8246 0 0 2 1 34.42 100.00 2.6055 1 0 2 6 35.19 96.19 2.5502 2 1 0 6 38.74 8.97 2.3243 3 -1 1 6 38.74 47.59 2.3243 2 1 1 6 39.40 9.47 2.2867 1 1 2 3 39.40 3.70 2.2867 2 -1 2 3 40.09 2.84 2.2491 3 0 0 6 41.71 27.86 2.1657 2 0 2 6 43.30 50.68 2.0896 3 0 1 6 46.63 1.29 1.9477 2 2 0 3 48.07 1.59 1.8929 2 1 2 6 48.66 3.99 1.8713 3 1 0 6 50.31 10.35 1.8138 1 0 3 6 51.44 17.14 1.7764 4 -1 1 6 55.92 6.84 1.6443 2 0 3 6 56.98 4.09 1.6163 4 0 1 6 57.47 21.16 1.6035 4 -2 2 3 57.47 6.57 1.6035 2 2 2 3 59.23 4.63 1.5600 4 -1 2 6 59.23 4.28 1.5600 3 1 2 6 59.74 3.49 1.5479 3 2 0 6 61.18 9.98 1.5148 3 -1 3 6 62.18 1.03 1.4929 5 -2 1 6 62.18 28.56 1.4929 3 2 1 6 63.15 2.39 1.4724 4 1 0 6 64.33 1.92 1.4482 4 0 2 6 64.54 26.06 1.4438 3 0 3 6 65.52 2.67 1.4248 4 1 1 6 65.52 19.03 1.4248 5 -1 1 6 66.17 15.73 1.4123 0 0 4 1 67.79 3.57 1.3823 1 0 4 6 69.21 13.06 1.3574 5 -2 2 6 69.21 18.77 1.3574 3 2 2 6 69.68 1.24 1.3494 5 0 0 6 70.99 3.98 1.3277 2 -1 4 3 71.01 4.17 1.3274 3 1 3 6 71.94 4.00 1.3125 5 0 1 6 72.38 12.64 1.3056 4 1 2 6 72.38 4.08 1.3056 5 -1 2 6 72.56 2.79 1.3028 2 0 4 6 72.84 15.30 1.2985 3 3 0 3 74.40 3.12 1.2751 4 2 0 6 75.70 2.48 1.2564 4 0 3 6 76.60 5.18 1.2438 6 -2 1 6 76.60 2.68 1.2438 4 2 1 6 77.21 9.02 1.2355 3 -1 4 6 77.21 4.71 1.2355 2 1 4 6 78.56 2.49 1.2176 5 0 2 6 79.01 1.08 1.2118 5 1 0 6 80.27 1.21 1.1960 3 0 4 6 80.29 10.86 1.1958 5 -2 3 6 80.29 2.01 1.1958 3 2 3 6 81.18 10.21 1.1849 5 1 1 6 83.11 6.63 1.1622 6 -2 2 6 83.11 2.68 1.1622 4 2 2 6 83.31 7.13 1.1599 4 1 3 6 87.61 2.29 1.1137 5 1 2 6 89.31 1.23 1.0969 5 0 3 6 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.