Nierite Billy M, Labbe J, Selvaraj A, Roult G Materials Research Bulletin 18 (1983) 921-934 Modifications structurales du nitrure de silicium en fonction de la temperature _cod_database_code 1001244 _database_code_amcsd 0014307 CELL PARAMETERS: 7.6018 7.6018 2.9066 90.000 90.000 120.000 SPACE GROUP: P6_3/m X-RAY WAVELENGTH: 1.541838 Cell Volume: 145.462 Density (g/cm3): 3.202 MAX. ABS. INTENSITY / VOLUME**2: 12.05647433 RIR: 1.226 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 13.45 47.13 6.5834 1 0 0 6 23.40 31.58 3.8009 1 1 0 6 27.09 91.33 3.2917 2 0 0 6 33.71 100.00 2.6590 1 0 1 12 36.10 96.43 2.4883 2 1 0 6 39.01 7.27 2.3089 1 1 1 12 41.13 2.28 2.1945 3 0 0 6 41.44 30.33 2.1788 2 0 1 12 47.86 5.53 1.9004 2 2 0 6 48.14 3.86 1.8902 2 1 1 12 49.95 11.87 1.8259 1 3 0 6 52.23 44.07 1.7514 3 0 1 12 57.98 13.60 1.5906 2 2 1 12 59.82 2.11 1.5461 1 3 1 12 59.82 3.55 1.5461 3 1 1 12 61.39 8.72 1.5103 2 3 0 6 61.39 6.50 1.5103 3 2 0 6 64.07 16.66 1.4533 0 0 2 2 64.91 4.55 1.4366 1 4 0 6 64.91 3.35 1.4366 4 1 0 6 65.13 1.83 1.4322 4 0 1 12 69.21 1.92 1.3575 1 1 2 12 70.23 41.24 1.3402 2 3 1 12 70.23 7.28 1.3402 3 2 1 12 70.88 7.89 1.3295 2 0 2 12 71.68 5.29 1.3167 5 0 0 6 73.54 21.20 1.2879 4 1 1 12 74.96 9.53 1.2670 3 3 0 6 75.80 18.42 1.2549 2 1 2 12 80.00 2.29 1.1994 5 0 1 12 81.38 1.72 1.1824 5 1 0 6 83.79 2.04 1.1544 2 2 2 12 84.76 5.46 1.1438 2 4 1 12 85.37 4.02 1.1371 1 3 2 12 89.48 5.90 1.0952 5 1 1 12 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.