Nierite Billy M, Labbe J, Selvaraj A, Roult G Materials Research Bulletin 18 (1983) 921-934 Modifications structurales du nitrure de silicium en fonction de la temperature _cod_database_code 1001249 _database_code_amcsd 0014312 CELL PARAMETERS: 7.6374 7.6374 2.9220 90.000 90.000 120.000 SPACE GROUP: P6_3/m X-RAY WAVELENGTH: 1.541838 Cell Volume: 147.605 Density (g/cm3): 3.156 MAX. ABS. INTENSITY / VOLUME**2: 13.58230361 RIR: 1.401 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 13.39 77.04 6.6142 1 0 0 6 23.29 13.33 3.8187 1 1 0 6 26.96 72.96 3.3071 2 0 0 6 33.53 100.00 2.6728 1 0 1 12 35.92 3.04 2.4999 1 2 0 6 35.92 82.65 2.4999 2 1 0 6 38.81 10.95 2.3206 1 1 1 12 41.23 16.19 2.1897 2 0 1 12 47.63 1.10 1.9094 2 2 0 6 47.89 2.02 1.8996 2 1 1 12 49.70 10.71 1.8344 1 3 0 6 49.70 1.33 1.8344 3 1 0 6 51.96 48.49 1.7600 3 0 1 12 55.58 1.37 1.6535 4 0 0 6 57.67 12.59 1.5984 2 2 1 12 59.50 7.16 1.5536 3 1 1 12 61.07 3.97 1.5174 3 2 0 6 61.07 5.70 1.5174 2 3 0 6 63.70 14.66 1.4610 0 0 2 2 64.57 2.98 1.4433 1 4 0 6 64.57 1.71 1.4433 4 1 0 6 65.42 1.35 1.4266 1 0 2 12 69.85 30.40 1.3466 2 3 1 12 69.85 11.03 1.3466 3 2 1 12 70.46 6.38 1.3364 2 0 2 12 71.29 4.29 1.3228 5 0 0 6 73.13 9.10 1.2941 4 1 1 12 74.55 14.83 1.2729 3 3 0 6 75.35 1.08 1.2614 1 2 2 12 75.35 15.61 1.2614 2 1 2 12 79.54 2.05 1.2051 5 0 1 12 80.93 1.45 1.1879 5 1 0 6 84.26 9.23 1.1492 2 4 1 12 84.84 3.57 1.1428 1 3 2 12 88.94 6.80 1.1005 5 1 1 12 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.