Mg2 Ni Soubeyroux J, Fruchart D, Mikou A, Pezat M, Darriet B Materials Research Bulletin 19 (1984) 895-904 Etude structurale du systeme Mg2 Ni - H2. I - La solution solide Mg2 Ni Hx (x=0.30) _cod_database_code 1008171 _database_code_amcsd 0016111 CELL PARAMETERS: 5.2050 5.2050 13.2360 90.000 90.000 120.000 SPACE GROUP: P6_222 X-RAY WAVELENGTH: 1.541838 Cell Volume: 310.548 Density (g/cm3): 3.442 MAX. ABS. INTENSITY / VOLUME**2: 38.61434810 RIR: 3.653 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 19.69 18.50 4.5077 1 0 0 6 20.13 53.58 4.4120 0 0 3 2 20.82 29.88 4.2670 1 0 1 12 23.88 15.70 3.7256 1 0 2 12 28.30 6.12 3.1530 1 0 3 12 35.14 1.56 2.5536 1 1 1 12 37.12 34.37 2.4220 1 1 2 12 39.48 34.96 2.2827 1 0 5 12 40.00 51.14 2.2538 2 0 0 6 40.23 10.42 2.2416 1 1 3 12 40.91 18.22 2.2060 0 0 6 2 44.28 5.94 2.0456 1 1 4 12 45.18 100.00 2.0071 2 0 3 12 45.79 9.33 1.9814 1 0 6 12 49.09 3.25 1.8558 1 1 5 12 52.48 3.60 1.7437 1 0 7 12 53.81 1.65 1.7037 2 1 0 12 54.29 3.99 1.6898 2 1 1 12 54.53 1.50 1.6828 1 1 6 12 55.71 2.39 1.6499 2 1 2 12 58.03 1.84 1.5894 2 1 3 12 58.55 9.63 1.5765 2 0 6 12 59.52 3.83 1.5532 1 0 8 12 63.49 5.82 1.4653 3 0 2 12 65.11 13.34 1.4327 2 1 5 12 65.64 2.01 1.4223 3 0 3 12 66.92 1.81 1.3981 1 0 9 12 67.03 8.76 1.3962 1 1 8 12 68.60 1.30 1.3681 3 0 4 12 69.74 3.73 1.3484 2 1 6 12 72.66 14.83 1.3012 2 2 0 6 74.04 3.00 1.2804 1 1 9 12 75.05 2.12 1.2657 2 1 7 12 76.29 5.63 1.2481 2 2 3 12 76.54 1.13 1.2447 3 1 1 12 77.50 5.13 1.2317 2 0 9 12 81.01 2.50 1.1869 2 1 8 12 81.60 3.22 1.1798 1 1 10 12 83.08 1.65 1.1626 1 0 11 12 85.99 5.00 1.1305 3 1 5 12 86.33 3.81 1.1269 4 0 0 6 86.92 8.49 1.1208 2 2 6 12 87.65 1.72 1.1133 2 1 9 12 87.75 3.49 1.1123 3 0 8 12 89.83 9.67 1.0919 4 0 3 12 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.