Ba Fe16.27 O27 Zn1.73 Collomb A, Vallet-Regi M Materials Research Bulletin 22 (1987) 753-760 Le zinc dans le ferrite hexagonal de type W: Ba Zn2 Fe16 O27 _cod_database_code 1008955 _database_code_amcsd 0016821 CELL PARAMETERS: 5.9333 5.9333 33.1160 90.000 90.000 120.000 SPACE GROUP: P6_3/mmc X-RAY WAVELENGTH: 1.541838 Cell Volume: 1009.627 Density (g/cm3): 5.233 MAX. ABS. INTENSITY / VOLUME**2: 41.53069723 RIR: 2.584 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.08 8.55 4.9075 1 0 2 12 19.05 5.73 4.6584 1 0 3 12 21.47 4.88 4.1395 0 0 8 2 23.66 1.41 3.7609 1 0 6 12 26.92 5.50 3.3116 0 0 10 2 29.87 15.24 2.9916 1 0 9 12 30.12 45.27 2.9667 1 1 0 6 30.62 2.06 2.9202 1 1 2 12 32.05 7.92 2.7928 1 1 4 12 32.16 58.56 2.7836 1 0 10 12 32.44 9.47 2.7597 0 0 12 2 34.32 100.00 2.6131 1 1 6 12 34.53 24.20 2.5975 1 0 11 12 34.92 1.20 2.5692 2 0 0 6 35.03 12.87 2.5615 2 0 1 12 35.35 8.28 2.5388 2 0 2 12 35.89 6.75 2.5023 2 0 3 12 36.62 29.26 2.4538 2 0 4 12 37.29 9.57 2.4113 1 1 8 12 37.55 9.08 2.3953 2 0 5 12 38.66 7.94 2.3292 2 0 6 12 39.93 1.64 2.2577 2 0 7 12 41.36 21.11 2.1829 2 0 8 12 42.05 2.27 2.1487 1 0 14 12 42.93 10.94 2.1065 2 0 9 12 44.64 1.05 2.0299 2 0 10 12 47.35 3.05 1.9199 1 0 16 12 48.41 1.73 1.8804 2 0 12 12 50.08 2.24 1.8215 1 0 17 12 50.45 2.54 1.8089 2 0 13 12 52.59 1.43 1.7402 2 0 14 12 53.34 5.86 1.7176 2 1 9 24 53.50 7.37 1.7128 3 0 0 6 54.02 1.98 1.6975 1 1 16 12 54.73 1.45 1.6773 3 0 4 12 54.80 21.92 1.6753 2 1 10 24 54.83 13.15 1.6744 2 0 15 12 55.50 5.23 1.6558 0 0 20 2 56.23 20.30 1.6358 3 0 6 12 56.38 14.35 1.6320 2 1 11 24 57.15 22.55 1.6118 2 0 16 12 58.30 2.27 1.5827 3 0 8 12 58.57 1.16 1.5760 1 0 20 12 59.08 1.42 1.5635 1 1 18 12 59.56 6.38 1.5523 2 0 17 12 61.81 2.01 1.5010 2 1 14 24 62.05 6.47 1.4958 2 0 18 12 62.63 42.85 1.4833 2 2 0 6 64.62 8.88 1.4424 2 0 19 12 65.96 1.74 1.4163 2 1 16 24 67.27 2.45 1.3918 2 0 20 12 68.18 2.27 1.3754 2 1 17 24 69.43 1.57 1.3537 2 2 10 12 70.00 2.30 1.3440 2 0 21 12 70.10 1.30 1.3424 1 1 22 12 70.92 1.72 1.3289 3 1 9 24 72.16 8.23 1.3091 3 1 10 24 72.32 4.21 1.3065 2 2 12 12 73.52 4.04 1.2881 3 1 11 24 73.82 1.20 1.2836 4 0 1 12 73.88 2.48 1.2827 1 0 25 12 74.79 2.96 1.2694 4 0 4 12 75.37 1.22 1.2611 4 0 5 12 76.08 1.28 1.2511 1 1 24 12 77.86 1.67 1.2269 4 0 8 12 81.36 1.06 1.1827 0 0 28 2 82.40 3.60 1.1704 1 1 26 12 87.92 1.51 1.1106 3 2 10 24 87.95 2.44 1.1103 4 0 15 12 88.50 6.40 1.1048 2 2 20 12 89.11 2.88 1.0988 4 1 6 24 89.57 2.20 1.0943 2 1 25 24 89.87 4.58 1.0915 4 0 16 12 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.