Cu3 Fe0.98 O9.12 Sb Ti0.96 Mouron P, Choisnet J Materials Research Bulletin 22 (1987) 1355-1362 A new ordered solid solution with a bixbyite structure: The compounds Cu2+x Ti2-x Fe2-x Sbx O9 (0< x < 1.4) _cod_database_code 1001689 _database_code_amcsd 0014321 CELL PARAMETERS: 9.5219 9.5219 9.5219 90.000 90.000 90.000 SPACE GROUP: Ia3 X-RAY WAVELENGTH: 1.541838 Cell Volume: 863.318 Density (g/cm3): 1.075 MAX. ABS. INTENSITY / VOLUME**2: 4.665698062 RIR: 1.413 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.64 12.23 4.7610 2 0 0 6 22.88 9.51 3.8873 2 1 1 24 26.48 3.46 3.3665 2 2 0 12 32.58 100.00 2.7487 2 2 2 8 35.27 1.06 2.5448 3 1 2 24 37.79 25.01 2.3805 4 0 0 6 42.46 2.24 2.1292 4 2 0 12 44.64 6.48 2.0301 3 3 2 24 46.74 5.48 1.9436 4 2 2 24 48.77 4.66 1.8674 4 3 1 24 48.77 4.46 1.8674 4 1 3 24 52.65 1.47 1.7385 5 1 2 24 54.52 33.37 1.6833 4 4 0 12 56.34 1.29 1.6330 4 3 3 24 58.13 1.93 1.5870 4 4 2 24 59.88 2.72 1.5447 6 1 1 24 61.60 2.04 1.5055 6 0 2 12 63.30 2.14 1.4693 5 4 1 24 63.30 2.59 1.4693 5 1 4 24 64.97 23.27 1.4355 6 2 2 24 66.61 1.54 1.4039 6 3 1 24 66.61 1.85 1.4039 6 1 3 24 68.24 4.94 1.3744 4 4 4 8 71.44 2.27 1.3204 6 0 4 12 73.02 1.25 1.2958 7 2 1 24 74.58 2.10 1.2724 6 4 2 24 80.74 2.81 1.1902 8 0 0 6 82.26 1.30 1.1721 8 1 1 24 83.77 1.63 1.1547 8 2 0 12 85.28 1.03 1.1381 6 5 3 24 86.78 1.87 1.1222 8 2 2 24 89.79 5.77 1.0922 6 6 2 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.