Al4.05 Ba Fe7.95 O19 Sandiumenge F, Gali S, Rodriguez J Materials Research Bulletin 23 (1988) 685-692 X-ray profile analysis of cation distribution in SrAlxFe12-xO19 solid solution _cod_database_code 1006003 _database_code_amcsd 0014327 CELL PARAMETERS: 5.7937 5.7937 22.7630 90.000 90.000 120.000 SPACE GROUP: P6_3/mmc X-RAY WAVELENGTH: 1.541838 Cell Volume: 661.717 Density (g/cm3): 4.991 MAX. ABS. INTENSITY / VOLUME**2: 33.30862145 RIR: 2.173 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 7.77 8.78 11.3815 0 0 2 2 17.68 1.63 5.0175 1 0 0 6 18.10 8.66 4.8999 1 0 1 12 19.33 7.61 4.5912 1 0 2 12 23.45 11.82 3.7938 0 0 6 2 23.64 6.22 3.7635 1 0 4 12 26.44 1.40 3.3716 1 0 5 12 29.52 1.95 3.0262 1 0 6 12 30.87 51.10 2.8969 1 1 0 6 31.44 13.50 2.8454 0 0 8 2 31.88 14.80 2.8073 1 1 2 12 32.82 98.18 2.7289 1 0 7 12 34.75 100.00 2.5816 1 1 4 12 35.79 10.86 2.5087 2 0 0 6 36.02 2.86 2.4936 2 0 1 12 36.30 4.54 2.4751 1 0 8 12 36.68 2.35 2.4499 2 0 2 12 37.77 44.57 2.3819 2 0 3 12 39.12 1.09 2.3024 1 1 6 12 39.59 1.22 2.2763 0 0 10 2 39.92 2.69 2.2585 1 0 9 12 41.08 33.49 2.1972 2 0 5 12 43.23 17.41 2.0926 2 0 6 12 47.53 7.05 1.9130 1 0 11 12 48.15 1.09 1.8899 2 1 1 24 49.54 1.02 1.8398 2 1 3 24 50.74 1.47 1.7992 2 1 4 24 51.03 3.88 1.7898 1 1 10 12 51.29 8.29 1.7811 2 0 9 12 54.06 1.04 1.6963 2 1 6 24 54.43 3.59 1.6858 2 0 10 12 54.90 8.21 1.6725 3 0 0 6 55.54 2.56 1.6547 3 0 2 12 56.14 38.18 1.6382 2 1 7 24 56.61 6.39 1.6259 0 0 14 2 57.43 19.66 1.6046 3 0 4 12 57.75 42.67 1.5964 2 0 11 12 58.13 3.36 1.5870 1 1 12 12 58.49 4.07 1.5781 2 1 8 24 61.07 1.47 1.5173 2 1 9 24 61.26 2.31 1.5131 2 0 12 12 64.11 1.68 1.4526 1 0 15 12 64.31 42.40 1.4484 2 2 0 6 64.95 2.41 1.4359 2 0 13 12 65.87 2.05 1.4179 1 1 14 12 66.93 4.61 1.3981 2 1 11 24 68.81 10.07 1.3644 2 0 14 12 69.46 2.26 1.3532 2 2 6 12 69.78 1.22 1.3478 3 0 10 12 73.34 5.21 1.2908 2 2 8 12 74.11 13.54 1.2794 3 1 7 24 74.27 2.44 1.2770 1 1 16 12 75.83 1.31 1.2545 3 0 12 12 77.06 4.32 1.2376 4 0 3 12 77.90 2.12 1.2263 1 0 18 12 79.21 2.52 1.2093 4 0 5 12 80.68 1.40 1.1910 4 0 6 12 81.18 1.47 1.1849 2 1 15 24 81.48 1.40 1.1813 2 0 17 12 83.39 6.11 1.1590 1 1 18 12 83.76 2.11 1.1548 3 1 11 24 85.27 1.43 1.1381 0 0 20 2 86.63 1.17 1.1238 4 0 9 12 89.51 1.11 1.0949 4 1 0 12 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.