Al6.36 Ba Fe5.64 O19 Sandiumenge F, Gali S, Rodriguez J Materials Research Bulletin 23 (1988) 685-692 X-ray profile analysis of cation distribution in SrAlxFe12-xO19 solid solution _cod_database_code 1006004 _database_code_amcsd 0014328 CELL PARAMETERS: 5.7473 5.7473 22.5850 90.000 90.000 120.000 SPACE GROUP: P6_3/mmc X-RAY WAVELENGTH: 1.541838 Cell Volume: 646.068 Density (g/cm3): 4.769 MAX. ABS. INTENSITY / VOLUME**2: 29.04064915 RIR: 1.983 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 7.83 17.16 11.2925 0 0 2 2 15.69 2.54 5.6462 0 0 4 2 17.82 3.09 4.9773 1 0 0 6 18.25 9.94 4.8607 1 0 1 12 19.49 6.80 4.5545 1 0 2 12 21.40 2.90 4.1519 1 0 3 12 23.64 11.65 3.7642 0 0 6 2 23.83 6.87 3.7337 1 0 4 12 26.65 2.31 3.3449 1 0 5 12 29.76 1.78 3.0023 1 0 6 12 31.12 57.33 2.8737 1 1 0 6 31.69 12.48 2.8231 0 0 8 2 32.14 17.32 2.7849 1 1 2 12 33.09 97.67 2.7074 1 0 7 12 35.04 100.00 2.5610 1 1 4 12 36.09 9.49 2.4887 2 0 0 6 36.59 3.40 2.4556 1 0 8 12 36.99 2.69 2.4303 2 0 2 12 38.08 39.29 2.3629 2 0 3 12 39.57 2.39 2.2773 2 0 4 12 39.92 2.96 2.2585 0 0 10 2 40.25 3.15 2.2408 1 0 9 12 41.42 36.53 2.1797 2 0 5 12 43.60 17.74 2.0760 2 0 6 12 45.01 1.30 2.0139 1 1 8 12 47.93 8.65 1.8980 1 0 11 12 48.56 1.28 1.8748 2 1 1 24 49.97 1.93 1.8251 2 1 3 24 51.18 1.51 1.7848 2 1 4 24 51.46 4.33 1.7757 1 1 10 12 51.73 8.79 1.7670 2 0 9 12 54.90 3.10 1.6725 2 0 10 12 55.38 9.16 1.6591 3 0 0 6 56.02 2.98 1.6415 3 0 2 12 56.64 38.45 1.6252 2 1 7 24 57.09 5.99 1.6132 0 0 14 2 57.93 19.65 1.5918 3 0 4 12 58.26 41.46 1.5838 2 0 11 12 58.63 3.56 1.5745 1 1 12 12 59.00 3.48 1.5655 2 1 8 24 61.62 1.70 1.5052 2 1 9 24 61.80 2.09 1.5011 2 0 12 12 64.68 1.77 1.4412 1 0 15 12 64.90 42.30 1.4368 2 2 0 6 65.53 1.92 1.4245 2 0 13 12 66.46 2.73 1.4067 1 1 14 12 67.53 5.54 1.3870 2 1 11 24 69.43 9.76 1.3537 2 0 14 12 70.10 2.21 1.3424 2 2 6 12 70.42 1.36 1.3371 3 0 10 12 74.03 4.89 1.2805 2 2 8 12 74.81 13.57 1.2692 3 1 7 24 74.96 2.53 1.2670 1 1 16 12 76.55 1.39 1.2446 3 0 12 12 77.80 3.92 1.2277 4 0 3 12 78.64 2.07 1.2167 1 0 18 12 79.98 2.72 1.1996 4 0 5 12 81.46 1.40 1.1814 4 0 6 12 81.96 1.58 1.1755 2 1 15 24 82.26 1.23 1.1720 2 0 17 12 83.60 1.21 1.1566 3 0 14 12 84.20 6.32 1.1499 1 1 18 12 84.59 2.57 1.1456 3 1 11 24 86.11 1.49 1.1292 0 0 20 2 87.50 1.24 1.1148 4 0 9 12 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.