Al8.56 Ba Fe3.44 O19 Sandiumenge F, Gali S, Rodriguez J Materials Research Bulletin 23 (1988) 685-692 X-ray profile analysis of cation distribution in SrAlxFe12-xO19 solid solution _cod_database_code 1006005 _database_code_amcsd 0014329 CELL PARAMETERS: 5.6916 5.6916 22.4030 90.000 90.000 120.000 SPACE GROUP: P6_3/mmc X-RAY WAVELENGTH: 1.541838 Cell Volume: 628.500 Density (g/cm3): 4.567 MAX. ABS. INTENSITY / VOLUME**2: 25.46004440 RIR: 1.815 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 7.89 25.05 11.2015 0 0 2 2 15.82 6.88 5.6007 0 0 4 2 18.00 3.45 4.9291 1 0 0 6 18.43 14.03 4.8139 1 0 1 12 19.68 8.18 4.5116 1 0 2 12 21.60 6.60 4.1137 1 0 3 12 23.83 11.73 3.7338 0 0 6 2 24.05 6.41 3.7002 1 0 4 12 26.89 3.78 3.3155 1 0 5 12 31.44 61.23 2.8458 1 1 0 6 31.96 12.38 2.8004 0 0 8 2 32.46 18.72 2.7582 1 1 2 12 33.38 93.20 2.6842 1 0 7 12 35.38 100.00 2.5371 1 1 4 12 36.46 7.44 2.4645 2 0 0 6 36.92 2.50 2.4349 1 0 8 12 37.36 2.52 2.4070 2 0 2 12 38.46 34.77 2.3404 2 0 3 12 39.97 4.67 2.2558 2 0 4 12 40.26 5.42 2.2403 0 0 10 2 40.60 3.65 2.2220 1 0 9 12 41.83 40.60 2.1594 2 0 5 12 44.02 19.87 2.0569 2 0 6 12 45.44 2.49 1.9960 1 1 8 12 48.36 9.74 1.8823 1 0 11 12 49.07 1.84 1.8566 2 1 1 24 50.49 3.13 1.8076 2 1 3 24 51.71 1.32 1.7678 2 1 4 24 51.95 4.75 1.7603 1 1 10 12 52.23 9.36 1.7514 2 0 9 12 53.25 1.31 1.7202 2 1 5 24 55.43 2.35 1.6578 2 0 10 12 55.97 9.72 1.6430 3 0 0 6 56.62 3.20 1.6256 3 0 2 12 57.21 37.21 1.6101 2 1 7 24 57.60 5.40 1.6002 0 0 14 2 58.55 19.62 1.5766 3 0 4 12 58.82 39.69 1.5699 2 0 11 12 59.19 4.11 1.5610 1 1 12 12 59.60 3.00 1.5511 2 1 8 24 62.24 1.95 1.4915 2 1 9 24 62.40 1.94 1.4881 2 0 12 12 65.28 1.93 1.4294 1 0 15 12 65.61 41.77 1.4229 2 2 0 6 66.17 1.42 1.4123 2 0 13 12 67.10 3.12 1.3948 1 1 14 12 68.22 6.14 1.3746 2 1 11 24 70.12 9.71 1.3421 2 0 14 12 70.87 2.20 1.3296 2 2 6 12 71.16 1.49 1.3249 3 0 10 12 74.85 4.88 1.2685 2 2 8 12 75.64 13.08 1.2572 3 1 7 24 75.70 2.71 1.2564 1 1 16 12 77.37 1.61 1.2334 3 0 12 12 78.70 3.59 1.2158 4 0 3 12 79.41 2.05 1.2067 1 0 18 12 79.86 1.01 1.2011 2 2 10 12 80.91 2.99 1.1882 4 0 5 12 82.42 1.56 1.1702 4 0 6 12 82.84 1.75 1.1653 2 1 15 24 83.12 1.17 1.1621 2 0 17 12 84.52 1.39 1.1464 3 0 14 12 85.07 6.14 1.1403 1 1 18 12 85.56 2.89 1.1351 3 1 11 24 86.98 1.60 1.1201 0 0 20 2 88.54 1.32 1.1044 4 0 9 12 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.