Al9.86 Ba Fe2.14 O19 Sandiumenge F, Gali S, Rodriguez J Materials Research Bulletin 23 (1988) 685-692 X-ray profile analysis of cation distribution in SrAlxFe12-xO19 solid solution _cod_database_code 1006006 _database_code_amcsd 0014330 CELL PARAMETERS: 5.6286 5.6286 22.2030 90.000 90.000 120.000 SPACE GROUP: P6_3/mmc X-RAY WAVELENGTH: 1.541838 Cell Volume: 609.176 Density (g/cm3): 4.508 MAX. ABS. INTENSITY / VOLUME**2: 22.49897291 RIR: 1.625 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 7.96 28.34 11.1015 0 0 2 2 15.97 4.88 5.5507 0 0 4 2 18.20 3.30 4.8745 1 0 0 6 18.64 23.74 4.7611 1 0 1 12 19.89 15.85 4.4632 1 0 2 12 21.83 7.44 4.0709 1 0 3 12 24.05 14.36 3.7005 0 0 6 2 24.30 8.08 3.6627 1 0 4 12 27.16 6.20 3.2827 1 0 5 12 31.80 55.95 2.8143 1 1 0 6 32.25 14.01 2.7754 0 0 8 2 32.83 20.77 2.7280 1 1 2 12 33.71 92.27 2.6586 1 0 7 12 35.77 100.00 2.5101 1 1 4 12 36.88 7.74 2.4373 2 0 0 6 37.28 1.68 2.4118 1 0 8 12 37.79 1.70 2.3806 2 0 2 12 38.90 38.02 2.3150 2 0 3 12 40.42 6.03 2.2316 2 0 4 12 40.63 6.51 2.2203 0 0 10 2 41.00 4.76 2.2012 1 0 9 12 42.30 49.18 2.1366 2 0 5 12 44.51 26.47 2.0354 2 0 6 12 44.86 1.27 2.0206 1 0 10 12 45.92 2.95 1.9761 1 1 8 12 48.84 9.16 1.8649 1 0 11 12 49.65 3.07 1.8361 2 1 1 24 51.09 3.51 1.7878 2 1 3 24 52.32 1.62 1.7486 2 1 4 24 52.50 5.31 1.7431 1 1 10 12 52.80 11.21 1.7338 2 0 9 12 53.88 2.00 1.7017 2 1 5 24 56.03 2.03 1.6413 2 0 10 12 56.65 8.86 1.6248 3 0 0 6 57.31 3.52 1.6077 3 0 2 12 57.88 37.03 1.5931 2 1 7 24 58.17 5.42 1.5859 0 0 14 2 59.26 19.59 1.5594 3 0 4 12 59.46 41.69 1.5546 2 0 11 12 59.82 4.84 1.5460 1 1 12 12 60.30 2.57 1.5350 2 1 8 24 62.97 2.49 1.4762 2 1 9 24 63.08 1.77 1.4737 2 0 12 12 65.88 1.13 1.4178 2 1 10 24 65.95 2.21 1.4163 1 0 15 12 66.44 43.45 1.4072 2 2 0 6 66.90 1.23 1.3987 2 0 13 12 67.83 2.74 1.3817 1 1 14 12 69.02 5.82 1.3608 2 1 11 24 69.68 1.17 1.3494 3 1 1 24 70.89 10.94 1.3293 2 0 14 12 71.77 2.64 1.3153 2 2 6 12 72.02 1.65 1.3112 3 0 10 12 75.80 5.47 1.2551 2 2 8 12 76.55 3.04 1.2446 1 1 16 12 76.61 13.02 1.2437 3 1 7 24 78.31 1.89 1.2209 3 0 12 12 79.48 1.01 1.2059 2 0 16 12 79.75 3.94 1.2024 4 0 3 12 80.28 2.21 1.1958 1 0 18 12 80.88 1.21 1.1886 2 2 10 12 81.12 1.09 1.1856 3 1 9 24 81.99 3.61 1.1752 4 0 5 12 83.52 2.09 1.1575 4 0 6 12 83.84 2.00 1.1539 2 1 15 24 84.08 1.52 1.1512 2 0 17 12 85.57 1.23 1.1349 3 0 14 12 86.06 5.94 1.1297 1 1 18 12 86.68 2.77 1.1233 3 1 11 24 87.96 1.89 1.1101 0 0 20 2 89.75 1.59 1.0926 4 0 9 12 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.