Sinoite Baraton M, Billy M, Labbe J, Quintard P, Roult G Materials Research Bulletin 23 (1988) 1087-1099 L'Oxynitrure de Silicium : Si2 N2 O II. Evolution Structurale et Endommagement par Irradiation aux Neutrons Rapides _cod_database_code 1001785 _database_code_amcsd 0014334 CELL PARAMETERS: 8.8709 5.4907 4.8500 90.000 90.000 90.000 SPACE GROUP: Cmc2_1 X-RAY WAVELENGTH: 1.541838 Cell Volume: 236.231 Density (g/cm3): 2.816 MAX. ABS. INTENSITY / VOLUME**2: 12.90790275 RIR: 1.492 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 19.01 50.48 4.6687 1 1 0 4 20.02 100.00 4.4355 2 0 0 2 26.50 98.02 3.3636 1 1 1 4 32.62 15.81 2.7453 0 2 0 2 34.45 30.57 2.6034 3 1 0 4 37.07 41.79 2.4250 0 0 2 1 37.65 35.89 2.3891 0 2 1 2 39.28 21.02 2.2938 3 1 1 4 40.68 3.11 2.2177 4 0 0 2 41.98 5.97 2.1520 1 1 2 4 42.48 5.04 2.1278 2 0 2 2 43.00 12.71 2.1034 2 2 1 4 50.20 6.60 1.8175 0 2 2 2 50.95 7.81 1.7925 1 3 0 4 51.50 8.50 1.7745 3 1 2 4 54.34 9.00 1.6882 5 1 0 4 56.21 2.19 1.6365 4 0 2 2 56.63 2.52 1.6254 4 2 1 4 57.83 14.94 1.5944 5 1 1 4 59.39 11.28 1.5562 3 3 0 4 60.61 7.17 1.5277 1 1 3 4 62.70 1.91 1.4818 3 3 1 4 62.86 4.80 1.4785 6 0 0 2 64.66 5.04 1.4414 1 3 2 4 67.20 14.33 1.3931 0 2 3 2 67.61 3.83 1.3855 5 1 2 4 68.29 10.82 1.3734 3 1 3 4 68.34 3.56 1.3727 0 4 0 2 70.91 10.13 1.3291 2 2 3 4 71.42 4.47 1.3208 0 4 1 2 72.02 5.48 1.3113 2 4 0 4 72.12 8.41 1.3097 3 3 2 4 72.63 1.57 1.3017 6 2 0 4 74.48 7.46 1.2739 5 3 0 4 75.28 6.57 1.2624 6 0 2 2 75.64 10.60 1.2572 6 2 1 4 78.96 1.58 1.2125 0 0 4 1 80.22 1.22 1.1966 7 1 1 4 80.38 1.70 1.1946 0 4 2 2 82.64 8.37 1.1676 5 1 3 4 83.88 2.99 1.1535 2 4 2 4 84.47 1.78 1.1469 6 2 2 4 86.25 5.83 1.1278 5 3 2 4 86.88 1.48 1.1212 3 3 3 4 88.09 1.14 1.1089 8 0 0 2 89.08 1.40 1.0991 3 1 4 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.