Heklaite Fischer J, Kramer V Materials Research Bulletin 26 (1991) 925-930 Crystal structure of KNaSiF_6_ Locality: synthetic _database_code_amcsd 0014361 CELL PARAMETERS: 9.3246 5.4992 9.7892 90.000 90.000 90.000 SPACE GROUP: Pnma X-RAY WAVELENGTH: 1.541838 Cell Volume: 501.969 Density (g/cm3): 2.701 MAX. ABS. INTENSITY / VOLUME**2: 8.077592381 RIR: 0.974 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 13.11 9.91 6.7518 1 0 1 4 18.12 22.39 4.8946 0 0 2 2 18.51 1.01 4.7945 0 1 1 4 19.04 8.30 4.6623 2 0 0 2 20.49 51.63 4.3338 1 0 2 4 20.83 69.88 4.2639 1 1 1 8 26.18 43.64 3.4038 1 1 2 8 26.40 42.27 3.3759 2 0 2 4 26.67 100.00 3.3425 2 1 1 8 28.99 2.82 3.0799 1 0 3 4 30.17 8.47 2.9625 3 0 1 4 31.89 9.80 2.8062 0 1 3 4 32.57 15.40 2.7496 0 2 0 2 34.39 10.91 2.6081 3 1 1 8 35.24 2.23 2.5465 1 2 1 8 37.40 1.66 2.4043 2 1 3 8 37.52 1.93 2.3972 0 2 2 4 37.99 1.93 2.3684 2 2 0 4 38.00 3.13 2.3681 3 1 2 8 38.01 2.70 2.3671 1 0 4 4 38.62 2.21 2.3312 4 0 0 2 39.13 24.35 2.3020 2 2 1 8 40.06 19.43 2.2506 3 0 3 4 41.53 5.06 2.1743 1 1 4 8 41.68 1.42 2.1669 2 0 4 4 42.10 1.51 2.1463 4 1 0 4 42.40 1.65 2.1319 2 2 2 8 42.97 4.25 2.1046 4 0 2 4 43.15 8.46 2.0965 4 1 1 8 44.15 42.46 2.0511 1 2 3 8 44.96 3.44 2.0160 2 1 4 8 44.98 24.34 2.0153 3 2 1 8 46.18 1.97 1.9656 4 1 2 8 47.27 11.18 1.9228 3 0 4 4 47.43 2.36 1.9167 2 2 3 8 47.45 9.72 1.9161 1 0 5 4 47.92 10.97 1.8982 3 2 2 8 49.41 5.07 1.8444 0 1 5 4 49.77 5.87 1.8320 5 0 1 4 50.27 13.83 1.8151 3 1 4 8 50.56 7.32 1.8051 2 0 5 4 50.93 2.62 1.7932 4 1 3 8 51.39 4.70 1.7781 4 2 0 4 52.51 1.02 1.7427 5 0 2 4 52.55 2.29 1.7416 3 2 3 8 54.34 1.53 1.6883 1 3 2 8 54.61 7.65 1.6806 2 3 1 8 54.94 1.68 1.6712 4 2 2 8 55.30 2.42 1.6613 5 1 2 8 55.47 1.11 1.6566 3 0 5 4 57.68 1.07 1.5982 0 3 3 4 58.58 5.09 1.5757 3 2 4 8 58.73 1.98 1.5720 1 2 5 8 59.28 3.04 1.5588 3 3 1 8 59.48 1.29 1.5541 6 0 0 2 59.52 1.27 1.5532 5 1 3 8 60.08 2.13 1.5400 2 0 6 4 61.73 1.02 1.5027 3 3 2 8 62.06 1.56 1.4955 6 1 0 4 62.63 1.48 1.4833 5 0 4 4 62.86 1.15 1.4784 6 1 1 8 63.17 5.49 1.4720 5 2 2 8 64.41 1.06 1.4464 4 1 5 8 64.81 1.33 1.4385 4 2 4 8 66.66 1.94 1.4031 0 2 6 4 66.66 1.35 1.4031 6 0 3 4 67.08 1.10 1.3952 5 2 3 8 67.80 1.50 1.3823 4 3 2 8 68.22 5.20 1.3748 0 4 0 2 69.63 1.46 1.3504 5 0 5 4 70.03 5.62 1.3436 2 2 6 8 70.36 2.13 1.3381 0 3 5 4 71.05 4.38 1.3268 3 3 4 8 72.01 1.78 1.3114 5 1 5 8 72.48 2.99 1.3040 6 2 2 8 73.02 1.29 1.2958 5 3 1 8 74.52 1.50 1.2733 2 4 2 8 75.23 1.39 1.2630 5 3 2 8 76.17 2.62 1.2498 6 2 3 8 78.59 1.42 1.2172 6 0 5 4 81.13 1.21 1.1854 6 3 0 4 82.29 1.35 1.1717 4 1 7 8 86.49 1.14 1.1253 7 2 3 8 87.16 1.44 1.1183 3 4 4 8 87.19 2.43 1.1179 0 2 8 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.