La2 Li O6 Sb Lopez M, Veiga M, Rodriguez-Carvajal J, Fernandez F, Jerez A, Pico C Materials Research Bulletin 27 (1992) 647-654 The monoclinic perovskite La2LiSbO6. A Rietveld refinement of neutron powder diffraction data _cod_database_code 1006046 _database_code_amcsd 0014366 CELL PARAMETERS: 5.6226 5.7199 7.9689 90.000 89.796 90.000 SPACE GROUP: P2_1/n X-RAY WAVELENGTH: 1.541838 Cell Volume: 256.284 Density (g/cm3): 6.511 MAX. ABS. INTENSITY / VOLUME**2: 80.55786591 RIR: 4.029 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 19.10 50.82 4.6468 0 1 1 4 19.29 14.35 4.6019 1 0 1 2 19.35 25.83 4.5864 -1 0 1 2 22.17 21.94 4.0097 1 1 0 4 22.31 13.07 3.9844 0 0 2 2 24.83 8.01 3.5855 1 1 1 4 24.88 8.24 3.5782 -1 1 1 4 31.28 45.66 2.8600 0 2 0 2 31.62 100.00 2.8299 1 1 2 4 31.70 99.89 2.8227 -1 1 2 4 31.83 48.96 2.8113 2 0 0 2 33.28 10.45 2.6918 0 2 1 4 37.01 8.54 2.4291 1 2 1 4 37.04 4.57 2.4268 -1 2 1 4 37.33 4.86 2.4092 0 1 3 4 37.35 17.07 2.4076 2 1 1 4 37.39 1.77 2.4051 1 0 3 2 37.42 1.56 2.4031 -2 1 1 4 37.50 7.93 2.3984 -1 0 3 2 38.76 14.02 2.3234 0 2 2 4 39.15 8.37 2.3009 2 0 2 2 39.29 8.65 2.2932 -2 0 2 2 40.70 2.93 2.2170 1 1 3 4 40.80 3.17 2.2119 -1 1 3 4 45.23 46.94 2.0049 2 2 0 4 45.53 27.69 1.9922 0 0 4 2 46.67 5.97 1.9463 0 2 3 4 46.69 5.17 1.9454 2 2 1 4 46.75 4.91 1.9431 -2 2 1 4 49.13 2.84 1.8543 0 3 1 4 49.52 5.43 1.8407 1 2 3 4 49.61 1.71 1.8377 -1 2 3 4 49.93 4.41 1.8264 -2 1 3 4 50.03 1.37 1.8230 -3 0 1 2 51.05 1.13 1.7891 -2 2 2 4 51.15 2.10 1.7859 1 1 4 4 51.26 1.64 1.7823 -1 1 4 4 51.30 2.23 1.7810 3 1 0 4 51.91 8.15 1.7614 1 3 1 4 51.94 7.06 1.7606 -1 3 1 4 52.70 1.26 1.7369 -3 1 1 4 55.88 12.15 1.6454 1 3 2 4 55.93 11.31 1.6439 -1 3 2 4 56.28 17.01 1.6347 0 2 4 4 56.52 8.82 1.6282 2 0 4 2 56.53 20.22 1.6280 3 1 2 4 56.68 19.30 1.6239 -3 1 2 4 56.73 10.07 1.6227 -2 0 4 2 57.52 1.61 1.6022 2 2 3 4 57.68 1.66 1.5983 -2 2 3 4 59.70 1.01 1.5489 0 3 3 4 59.72 3.20 1.5485 2 3 1 4 60.20 2.23 1.5372 -3 2 1 4 60.28 2.60 1.5353 0 1 5 4 60.34 1.77 1.5340 3 0 3 2 60.43 1.22 1.5319 -1 0 5 2 62.13 3.34 1.4941 1 3 3 4 62.20 3.79 1.4925 -1 3 3 4 65.25 3.38 1.4300 0 4 0 2 66.03 10.67 1.4150 2 2 4 4 66.22 10.92 1.4114 -2 2 4 4 66.42 4.01 1.4075 0 4 1 4 66.52 5.68 1.4056 4 0 0 2 68.76 1.03 1.3652 -1 4 1 4 69.33 1.83 1.3554 -2 3 3 4 69.51 1.28 1.3524 1 2 5 4 69.54 1.15 1.3518 3 2 3 4 69.68 2.76 1.3494 2 1 5 4 69.75 1.26 1.3483 -3 2 3 4 69.87 2.71 1.3462 4 1 1 4 71.55 1.82 1.3187 3 3 1 4 71.62 1.96 1.3176 -3 3 1 4 74.44 2.82 1.2746 2 4 0 4 74.88 3.85 1.2682 3 3 2 4 75.01 3.95 1.2662 -3 3 2 4 75.32 6.18 1.2617 1 1 6 4 75.34 4.70 1.2615 4 2 0 4 75.46 6.19 1.2598 -1 1 6 4 75.51 1.70 1.2591 0 4 3 4 75.52 2.20 1.2589 2 4 1 4 75.57 2.21 1.2583 -2 4 1 4 76.22 1.10 1.2491 2 2 5 4 76.44 1.06 1.2461 -2 2 5 4 78.97 1.65 1.2124 -4 1 3 4 80.30 1.62 1.1956 1 3 5 4 80.34 1.58 1.1952 3 3 3 4 80.41 1.72 1.1942 -1 3 5 4 80.53 1.68 1.1927 -3 3 3 4 83.15 2.63 1.1617 0 4 4 4 84.15 2.33 1.1505 4 0 4 2 84.20 2.11 1.1499 2 4 3 4 84.33 2.07 1.1484 -2 4 3 4 84.50 2.47 1.1466 -4 0 4 2 86.93 1.06 1.1206 4 3 1 4 87.96 1.86 1.1102 1 5 1 4 87.98 2.35 1.1100 -1 5 1 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.