Si2 Ti Smith P, Ortega R, Brennan B Materials Research Society Symposia Proceedings 481 (1998) 605-610 Pseudo-C11b phase formation of titanium disilicide during the C49 to C54 transition _cod_database_code 1009012 _database_code_amcsd 0016874 CELL PARAMETERS: 4.4280 4.7790 9.0780 90.000 90.000 90.000 SPACE GROUP: Fmmm X-RAY WAVELENGTH: 1.541838 Cell Volume: 192.103 Density (g/cm3): 3.597 MAX. ABS. INTENSITY / VOLUME**2: 62.71794357 RIR: 5.678 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 19.56 1.70 4.5390 0 0 2 2 29.20 9.69 3.0582 1 1 1 8 37.64 26.12 2.3895 0 2 0 2 39.72 2.26 2.2695 0 0 4 2 40.75 79.59 2.2141 1 1 3 8 40.75 20.41 2.2140 2 0 0 2 55.87 1.34 1.6456 0 2 4 4 56.68 13.80 1.6240 2 2 0 4 58.21 1.15 1.5848 2 0 4 4 61.27 4.76 1.5130 0 0 6 2 70.05 13.04 1.3432 1 3 3 8 71.42 1.02 1.3207 2 2 4 8 74.18 4.98 1.2783 0 2 6 4 74.18 10.80 1.2783 3 1 3 8 76.22 4.57 1.2492 2 0 6 4 79.60 1.43 1.2044 1 1 7 8 80.37 2.16 1.1947 0 4 0 2 88.28 6.00 1.1070 2 2 6 8 88.28 1.67 1.1070 4 0 0 2 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.