Fluoro-pargasite Della Ventura G, Bellatreccia F, Camara F, Oberti R Mineralogical Magazine 78 (2014) 293-310 Crystal-chemistry and short-range order of fluoro-edenite and fluoro-pargasite: a combined X-ray diffraction and FTIR spectroscopic approach Note: Sample FK1 Locality: Edenville, Orange County, New York, USA _database_code_amcsd 0020430 9.862 17.998 5.2942 90 105.17 90 C2/m atom x y z occ Biso B(1,1) B(2,2) B(3,3) B(1,2) B(1,3) B(2,3) NaA 0 .5 0 .15 1.49 .0036 .0013 .0201 0 .0071 0 KA 0 .5 0 .026 1.49 .0036 .0013 .0201 0 .0071 0 NaAm .04528 .5 .10067 .15 2.52 .0037 .0035 .0160 0 .0017 0 KAm .04528 .5 .10067 .026 2.52 .0037 .0035 .0160 0 .0017 0 NaA2 0 .47294 0 .15 1.87 .0054 .0012 .0289 0 .0116 0 KA2 0 .47294 0 .026 1.87 .0054 .0012 .0289 0 .0116 0 MgM1 0 .08910 .5 .818 .54 .0015 .0004 .0061 0 .0012 0 AlM1 0 .08910 .5 .092 .54 .0015 .0004 .0061 0 .0012 0 TiM1 0 .08910 .5 .008 .54 .0015 .0004 .0061 0 .0012 0 ZnM1 0 .08910 .5 .002 .54 .0015 .0004 .0061 0 .0012 0 FeM1 0 .08910 .5 .074 .54 .0015 .0004 .0061 0 .0012 0 MgM2 0 .17601 0 .818 .50 .0012 .0003 .0064 0 .0010 0 AlM2 0 .17601 0 .092 .50 .0012 .0003 .0064 0 .0010 0 TiM2 0 .17601 0 .008 .50 .0012 .0003 .0064 0 .0010 0 ZnM2 0 .17601 0 .002 .50 .0012 .0003 .0064 0 .0010 0 FeM2 0 .17601 0 .074 .50 .0012 .0003 .0064 0 .0010 0 MgM3 0 0 0 .818 .51 .0014 .0003 .0056 0 .0006 0 AlM3 0 0 0 .092 .51 .0014 .0003 .0056 0 .0006 0 TiM3 0 0 0 .008 .51 .0014 .0003 .0056 0 .0006 0 ZnM3 0 0 0 .002 .51 .0014 .0003 .0056 0 .0006 0 FeM3 0 0 0 .074 .51 .0014 .0003 .0056 0 .0006 0 CaM4 0 .27916 .5 .76 .0022 .0005 .0097 0 .0026 0 SiT1 .28064 .08506 .30189 .825 .41 .0008 .0003 .0055 0 .0007 0 AlT1 .28064 .08506 .30189 .175 .41 .0008 .0003 .0055 0 .0007 0 SiT2 .29019 .17281 .81134 .825 .44 .0009 .0004 .0055 0 .0009 .0001 AlT2 .29019 .17281 .81134 .175 .44 .0009 .0004 .0055 0 .0009 .0001 O1 .10783 .08689 .21743 .68 .0015 .0006 .0069 -.0003 .0013 -.0003 O2 .11931 .17229 .73105 .62 .0011 .0004 .0085 0 .0007 .0002 O3 .10663 0 .71453 .4 .83 .0022 .0006 .0096 0 .0016 0 F3 .10663 0 .71453 .59 .83 .0022 .0006 .0096 0 .0016 0 Cl3 .10663 0 .71453 .015 .83 .0022 .0006 .0096 0 .0016 0 O4 .36594 .25021 .79092 .79 .0023 .0005 .0096 -.0002 .0023 -.0001 O5 .34955 .13877 .10874 .89 .0018 .0008 .0086 0 .0007 .0009 O6 .34470 .11753 .60525 .86 .0016 .0007 .0108 .0001 .0015 -.0008 O7 .34173 0 .28363 1.04 .0021 .0005 .0154 0 .0010 0 H .17631 0 .74434 .4 1.00 1.0000 0 0 0 0 0