Fluoro-edenite Della Ventura G, Bellatreccia F, Camara F, Oberti R Mineralogical Magazine 78 (2014) 293-310 Crystal-chemistry and short-range order of fluoro-edenite and fluoro-pargasite: a combined X-ray diffraction and FTIR spectroscopic approach Note: Sample C2552 Locality: Sterling Hill, Ogdensburg, New Jersey, USA _database_code_amcsd 0020431 9.865 18.026 5.2836 90 105.013 90 C2/m atom x y z occ Biso B(1,1) B(2,2) B(3,3) B(1,2) B(1,3) B(2,3) NaA 0 .5 0 .176 2.24 .0067 .0020 .0210 0 .0079 0 KA 0 .5 0 .01 2.24 .0067 .0020 .0210 0 .0079 0 NaAm .04635 .5 .10415 .176 2.10 .0046 .0025 .0148 0 .0038 0 KAm .04635 .5 .10415 .01 2.10 .0046 .0025 .0148 0 .0038 0 NaA2 0 .47156 0 .176 2.77 .0099 .0008 .0505 0 .0207 0 KA2 0 .47156 0 .01 2.77 .0099 .0008 .0505 0 .0207 0 MgM1 0 .08864 .5 .868 .53 .0018 .0004 .0042 0 .0011 0 AlM1 0 .08864 .5 .018 .53 .0018 .0004 .0042 0 .0011 0 Fe3+M1 0 .08864 .5 .01 .53 .0018 .0004 .0042 0 .0011 0 TiM1 0 .08864 .5 .008 .53 .0018 .0004 .0042 0 .0011 0 ZnM1 0 .08864 .5 .002 .53 .0018 .0004 .0042 0 .0011 0 Fe2+M1 0 .08864 .5 .098 .53 .0018 .0004 .0042 0 .0011 0 MnM1 0 .08864 .5 .002 .53 .0018 .0004 .0042 0 .0011 0 MgM2 0 .17620 0 .868 .49 .0015 .0004 .0046 0 .0010 0 AlM2 0 .17620 0 .018 .49 .0015 .0004 .0046 0 .0010 0 Fe3+M2 0 .17620 0 .01 .49 .0015 .0004 .0046 0 .0010 0 TiM2 0 .17620 0 .008 .49 .0015 .0004 .0046 0 .0010 0 ZnM2 0 .17620 0 .002 .49 .0015 .0004 .0046 0 .0010 0 Fe2+M2 0 .17620 0 .098 .49 .0015 .0004 .0046 0 .0010 0 MnM2 0 .17620 0 .002 .49 .0015 .0004 .0046 0 .0010 0 MgM3 0 0 0 .868 .54 .0017 .0004 .0049 0 .0007 0 AlM3 0 0 0 .018 .54 .0017 .0004 .0049 0 .0007 0 Fe3+M3 0 0 0 .01 .54 .0017 .0004 .0049 0 .0007 0 TiM3 0 0 0 .008 .54 .0017 .0004 .0049 0 .0007 0 ZnM3 0 0 0 .002 .54 .0017 .0004 .0049 0 .0007 0 Fe2+M3 0 0 0 .098 .54 .0017 .0004 .0049 0 .0007 0 MnM3 0 0 0 .002 .54 .0017 .0004 .0049 0 .0007 0 CaM4 0 .27848 .5 .48 .79 .0027 .0005 .0088 0 .0029 0 NaM4 0 .27848 .5 .0125 .79 .0027 .0005 .0088 0 .0029 0 CaM4' 0 .25755 .5 .48 .94 .9352 0 0 0 0 0 NaM4' 0 .25755 .5 .0125 .94 .9352 0 0 0 0 0 SiT1 .28091 .08455 .30040 .8575 .44 .0012 .0003 .0042 0 .0006 0 AlT1 .28091 .08455 .30040 .1425 .44 .0012 .0003 .0042 0 .0006 0 SiT2 .28960 .17200 .80821 .8575 .45 .0012 .0004 .0040 0 .0007 0 AlT2 .28960 .17200 .80821 .1425 .45 .0012 .0004 .0040 0 .0007 0 O1 .10962 .08564 .21880 .62 .0016 .0006 .0050 -.0001 .0008 -.0002 O2 .11978 .17135 .72712 .61 .0013 .0006 .0058 0 .0006 0 O3 .10625 0 .71453 .34 .86 .0025 .0007 .0080 0 .0015 0 F3 .10625 0 .71453 .655 .86 .0025 .0007 .0080 0 .0015 0 Cl3 .10625 0 .71453 .005 .86 .0025 .0007 .0080 0 .0015 0 O4 .36481 .24920 .78973 .79 .0026 .0005 .0078 -.0003 .0018 -.0001 O5 .34894 .13711 .10513 .93 .0019 .0010 .0076 0 .0007 .0010 O6 .34560 .11700 .60216 .86 .0018 .0008 .0090 0 .0011 -.0008 O7 .34273 0 .28313 1.02 .0024 .0007 .0124 0 .0013 0 H .19118 0 .75125 .34 1.00 1.0000 0 0 0 0 0