Fluoro-edenite Della Ventura G, Bellatreccia F, Camara F, Oberti R Mineralogical Magazine 78 (2014) 293-310 Crystal-chemistry and short-range order of fluoro-edenite and fluoro-pargasite: a combined X-ray diffraction and FTIR spectroscopic approach Note: Sample G405 Locality: Franklin Quarry, Franklin, New Jersey, USA _database_code_amcsd 0020433 9.866 17.987 5.2817 90 105.16 90 C2/m atom x y z occ Biso B(1,1) B(2,2) B(3,3) B(1,2) B(1,3) B(2,3) NaA 0 .5 0 .142 1.31 .0035 .0013 .0110 0 .0029 0 KA 0 .5 0 .04 1.31 .0035 .0013 .0110 0 .0029 0 NaAm .04096 .5 .09011 .142 1.79 .0035 .0020 .0158 0 .0037 0 KAm .04096 .5 .09011 .04 1.79 .0035 .0020 .0158 0 .0037 0 NaA2 0 .47381 0 .142 2.80 .0081 .0009 .0544 0 .0185 0 KA2 0 .47381 0 .04 2.80 .0081 .0009 .0544 0 .0185 0 MgM1 0 .08891 .5 .876 .54 .0016 .0004 .0053 0 .0012 0 AlM1 0 .08891 .5 .072 .54 .0016 .0004 .0053 0 .0012 0 TiM1 0 .08891 .5 .002 .54 .0016 .0004 .0053 0 .0012 0 ZnM1 0 .08891 .5 .002 .54 .0016 .0004 .0053 0 .0012 0 FeM1 0 .08891 .5 .04 .54 .0016 .0004 .0053 0 .0012 0 MgM2 0 .17599 0 .876 .48 .0014 .0003 .0051 0 .0010 0 AlM2 0 .17599 0 .072 .48 .0014 .0003 .0051 0 .0010 0 TiM2 0 .17599 0 .002 .48 .0014 .0003 .0051 0 .0010 0 ZnM2 0 .17599 0 .002 .48 .0014 .0003 .0051 0 .0010 0 FeM2 0 .17599 0 .04 .48 .0014 .0003 .0051 0 .0010 0 MgM3 0 0 0 .876 .56 .0017 .0004 .0051 0 .0007 0 AlM3 0 0 0 .072 .56 .0017 .0004 .0051 0 .0007 0 TiM3 0 0 0 .002 .56 .0017 .0004 .0051 0 .0007 0 ZnM3 0 0 0 .002 .56 .0017 .0004 .0051 0 .0007 0 FeM3 0 0 0 .04 .56 .0017 .0004 .0051 0 .0007 0 CaM4 0 .27890 .5 .985 .77 .0025 .0005 .0088 0 .0027 0 NaM4 0 .27890 .5 .015 .77 .0025 .0005 .0088 0 .0027 0 SiT1 .28035 .08485 .30195 .85 .45 .0011 .0004 .0048 0 .0006 0 AlT1 .28035 .08485 .30195 .15 .45 .0011 .0004 .0048 0 .0006 0 SiT2 .28958 .17255 .81030 .85 .47 .0012 .0004 .0048 0 .0009 .0001 AlT2 .28958 .17255 .81030 .15 .47 .0012 .0004 .0048 0 .0009 .0001 O1 .10841 .08626 .21841 .65 .0016 .0006 .0060 -.0002 .0012 -.0002 O2 .11929 .17170 .72925 .64 .0013 .0005 .0076 0 .0009 .0001 O3 .10541 0 .71403 .265 .83 .0024 .0006 .0084 0 .0016 0 F3 .10541 0 .71403 .73 .83 .0024 .0006 .0084 0 .0016 0 Cl3 .10541 0 .71403 .005 .83 .0024 .0006 .0084 0 .0016 0 O4 .36519 .24981 .79128 .81 .0025 .0006 .0090 -.0002 .0024 -.0002 O5 .34897 .13769 .10746 .92 .0018 .0010 .0078 .0001 .0007 .0011 O6 .34497 .11765 .60348 .86 .0019 .0007 .0095 0 .0013 -.0008 O7 .34135 0 .28689 1.06 .0022 .0007 .0138 0 .0007 0 H .17242 0 .77762 .265 1.00 1.0000 0 0 0 0 0