Na0.35 O3 W Haegg G Nature 135 (1935) 874-874 The Spinels and the Cubic Sodium - Tungsten Bronzes as New Examples of Structures with Vacant Lattice Points _cod_database_code 1010420 _database_code_amcsd 0017344 CELL PARAMETERS: 3.8130 3.8130 3.8130 90.000 90.000 90.000 SPACE GROUP: Pm3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 55.437 Density (g/cm3): 7.184 MAX. ABS. INTENSITY / VOLUME**2: 439.2758581 RIR: 19.909 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 23.33 100.00 3.8130 1 0 0 6 33.23 66.10 2.6962 1 1 0 12 41.00 13.08 2.2014 1 1 1 8 47.70 20.89 1.9065 2 0 0 6 53.76 37.11 1.7052 2 1 0 24 59.37 23.60 1.5567 2 1 1 24 69.76 11.09 1.3481 2 2 0 12 74.68 3.09 1.2710 3 0 0 6 74.68 12.35 1.2710 2 2 1 24 79.49 9.21 1.2058 3 1 0 24 84.22 5.15 1.1497 3 1 1 24 88.91 3.44 1.1007 2 2 2 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.