Bismoclite Bannister F Nature (London) 134 (1934) 856-857 Crystal structure of bismuth oxyhalides _cod_database_code 1011175 _database_code_amcsd 0018052 CELL PARAMETERS: 3.8900 3.8900 7.3700 90.000 90.000 90.000 SPACE GROUP: P4/nmm X-RAY WAVELENGTH: 1.541838 Cell Volume: 111.524 Density (g/cm3): 7.754 MAX. ABS. INTENSITY / VOLUME**2: 265.0399122 RIR: 11.129 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 12.01 57.66 7.3700 0 0 1 2 24.15 14.89 3.6850 0 0 2 2 25.90 100.00 3.4402 1 0 1 8 32.55 61.29 2.7506 1 1 0 4 33.50 95.71 2.6752 1 0 2 8 34.81 7.16 2.5770 1 1 1 8 36.58 10.36 2.4567 0 0 3 2 40.94 24.15 2.2043 1 1 2 8 46.70 26.84 1.9450 2 0 0 4 48.40 6.39 1.8806 2 0 1 8 49.47 1.55 1.8425 0 0 4 2 49.76 23.77 1.8323 1 1 3 8 53.25 6.30 1.7201 2 0 2 8 54.17 24.07 1.6931 2 1 1 16 55.16 20.54 1.6652 1 0 4 8 58.69 31.84 1.5732 2 1 2 16 60.48 5.22 1.5308 1 1 4 8 60.74 8.79 1.5249 2 0 3 8 63.07 1.45 1.4740 0 0 5 2 68.01 3.87 1.3784 1 0 5 8 68.19 7.15 1.3753 2 2 0 4 69.53 1.77 1.3520 2 2 1 8 70.39 1.90 1.3376 2 0 4 8 72.79 2.34 1.2992 1 1 5 8 73.50 2.12 1.2885 2 2 2 8 74.27 4.02 1.2771 3 0 1 8 75.10 13.98 1.2649 2 1 4 16 77.61 7.46 1.2301 3 1 0 8 77.75 2.11 1.2283 0 0 6 2 78.14 5.89 1.2232 3 0 2 8 78.89 1.23 1.2133 3 1 1 16 79.94 3.46 1.2001 2 2 3 8 82.03 2.31 1.1748 2 0 5 8 82.71 4.28 1.1668 3 1 2 16 86.55 3.46 1.1246 2 1 5 16 86.84 4.90 1.1216 1 1 6 8 88.99 6.54 1.0999 3 1 3 16 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.