Bi Na3 O8 P2 Mairesse G, Drache M, Nowogrocki G, Abraham F Phase Transition 27 (1990) 91-105 Order-disorder transition in Na3Bi(PO4)2 _cod_database_code 1004092 _database_code_amcsd 0014942 CELL PARAMETERS: 18.7100 7.1800 5.4290 90.000 90.000 90.000 SPACE GROUP: Pnam X-RAY WAVELENGTH: 1.541838 Cell Volume: 729.320 Density (g/cm3): 4.261 MAX. ABS. INTENSITY / VOLUME**2: 50.61455244 RIR: 3.868 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 9.45 1.56 9.3550 2 0 0 2 13.21 100.00 6.7034 1 1 0 4 15.56 7.53 5.6958 2 1 0 4 18.85 23.85 4.7084 3 1 0 4 18.90 55.03 4.6956 2 0 1 4 18.97 26.00 4.6775 4 0 0 2 20.51 3.54 4.3304 0 1 1 4 21.06 45.88 4.2189 1 1 1 8 22.63 9.08 3.9298 2 1 1 8 22.69 5.13 3.9192 4 1 0 4 24.80 3.21 3.5900 0 2 0 2 25.03 44.47 3.5570 3 1 1 8 25.13 1.22 3.5436 4 0 1 4 25.26 1.22 3.5257 1 2 0 4 26.87 16.10 3.3184 5 1 0 4 28.08 2.43 3.1777 4 1 1 8 28.69 10.66 3.1113 3 2 0 4 30.23 2.14 2.9569 1 2 1 8 31.27 1.13 2.8602 6 1 0 4 31.37 61.09 2.8520 2 2 1 8 31.41 32.94 2.8479 4 2 0 4 31.60 13.79 2.8314 5 1 1 8 33.00 29.27 2.7145 0 0 2 2 33.13 49.75 2.7040 6 0 1 4 33.19 7.59 2.6995 3 2 1 8 35.69 14.83 2.5160 1 1 2 8 35.85 1.38 2.5049 7 1 0 4 37.90 7.13 2.3740 1 3 0 4 38.27 4.33 2.3517 3 1 2 8 38.34 5.52 2.3478 4 0 2 4 38.49 1.35 2.3387 8 0 0 2 38.50 2.01 2.3380 5 2 1 8 38.84 1.11 2.3187 2 3 0 4 39.62 18.15 2.2745 7 1 1 8 40.37 1.40 2.2345 3 3 0 4 41.22 4.29 2.1900 0 3 1 4 41.52 3.24 2.1751 1 3 1 8 41.72 4.97 2.1652 0 2 2 4 41.82 12.63 2.1599 6 2 1 8 42.01 1.92 2.1509 1 2 2 8 42.07 1.63 2.1479 8 0 1 4 42.39 1.67 2.1323 2 3 1 8 43.05 11.91 2.1011 5 1 2 8 43.81 5.66 2.0663 3 3 1 8 44.28 5.05 2.0455 3 2 2 8 44.96 3.15 2.0162 5 3 0 4 45.42 6.49 1.9969 9 1 0 4 45.75 3.84 1.9834 4 3 1 8 46.20 21.94 1.9649 4 2 2 8 46.33 10.48 1.9596 8 2 0 4 47.91 2.44 1.8986 6 3 0 4 48.14 1.08 1.8901 5 3 1 8 49.51 1.36 1.8409 7 1 2 8 50.75 1.48 1.7990 9 2 0 4 50.87 2.80 1.7950 0 4 0 2 51.11 3.45 1.7870 1 3 2 8 51.12 2.34 1.7868 1 4 0 4 51.43 3.94 1.7767 2 0 3 4 51.58 3.40 1.7718 8 0 2 4 51.67 2.99 1.7689 10 0 1 4 51.86 2.82 1.7630 2 3 2 8 52.37 3.04 1.7471 1 1 3 8 53.09 1.43 1.7252 3 3 2 8 53.67 2.54 1.7077 9 2 1 8 54.03 3.51 1.6972 1 4 1 8 54.14 4.34 1.6940 7 3 1 8 54.31 3.25 1.6892 3 1 3 8 54.75 3.69 1.6767 2 4 1 8 54.78 1.26 1.6758 4 4 0 4 56.89 1.83 1.6186 5 3 2 8 56.89 1.16 1.6184 5 4 0 4 57.28 4.92 1.6085 9 1 2 8 57.67 1.20 1.5986 8 3 1 8 57.91 6.77 1.5924 2 2 3 8 58.05 6.03 1.5888 8 2 2 8 58.06 1.40 1.5888 5 1 3 8 58.14 5.03 1.5867 10 2 1 8 58.28 3.70 1.5832 11 1 1 8 58.84 1.06 1.5695 9 3 0 4 59.02 5.32 1.5652 6 0 3 4 59.05 1.11 1.5643 3 2 3 8 59.27 2.47 1.5592 12 0 0 2 59.41 1.65 1.5558 6 3 2 8 59.61 2.73 1.5510 5 4 1 8 61.98 1.65 1.4973 0 4 2 4 62.06 2.79 1.4955 6 4 1 8 62.20 1.51 1.4925 1 4 2 8 62.31 1.46 1.4902 7 4 0 4 63.41 2.84 1.4669 7 1 3 8 64.78 1.14 1.4392 1 3 3 8 64.89 1.02 1.4370 7 4 1 8 65.00 1.57 1.4348 6 2 3 8 65.80 1.38 1.4194 2 5 0 4 66.23 1.74 1.4112 13 1 0 4 66.49 1.06 1.4063 3 3 3 8 67.36 1.23 1.3901 5 4 2 8 69.14 1.11 1.3587 9 3 2 8 69.22 1.98 1.3572 0 0 4 2 69.53 3.08 1.3520 12 0 2 4 70.04 1.66 1.3433 11 3 1 8 70.80 1.32 1.3309 4 5 1 8 70.83 1.11 1.3303 1 1 4 8 72.34 1.49 1.3063 7 4 2 8 76.01 1.50 1.2521 13 1 2 8 77.98 1.97 1.2252 4 2 4 8 78.15 1.53 1.2230 10 2 3 8 78.28 1.18 1.2213 11 1 3 8 78.35 1.20 1.2204 14 2 1 8 80.06 1.33 1.1986 15 1 1 8 87.41 1.28 1.1158 8 2 4 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.