YBa2(Cu.95Fe.05)3O7 Roth G, Heger G, Renker B, Pannetier J, Caignaert V, Hervieu M, Raveau B Physica C 153 (1988) 972-973 Crystallographic study of the tetragonal high-Tc superconductor YBa2(Cu.95Fe.05)3O7 _cod_database_code 1001377 _database_code_amcsd 0015010 CELL PARAMETERS: 3.8630 3.8630 11.6260 90.000 90.000 90.000 SPACE GROUP: P4/mmm X-RAY WAVELENGTH: 1.541838 Cell Volume: 173.492 Density (g/cm3): 6.351 MAX. ABS. INTENSITY / VOLUME**2: 163.7673709 RIR: 8.396 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 7.60 1.66 11.6260 0 0 1 2 15.24 1.46 5.8130 0 0 2 2 22.95 2.97 3.8753 0 0 3 2 23.02 5.91 3.8630 1 0 0 4 27.73 8.66 3.2174 1 0 2 8 32.73 100.00 2.7359 1 0 3 8 32.79 52.04 2.7316 1 1 0 4 36.34 2.16 2.4722 1 1 2 8 38.73 6.43 2.3252 0 0 5 2 38.77 6.34 2.3225 1 0 4 8 40.40 10.86 2.2327 1 1 3 8 46.89 7.58 1.9377 0 0 6 2 47.05 29.51 1.9315 2 0 0 4 51.62 3.67 1.7706 1 1 5 8 53.01 1.00 1.7276 2 1 0 8 55.31 1.13 1.6609 0 0 7 2 55.49 2.13 1.6560 2 1 2 16 58.39 13.13 1.5804 1 1 6 8 58.49 31.55 1.5779 2 1 3 16 62.51 4.74 1.4858 2 0 5 8 62.55 2.41 1.4851 2 1 4 16 65.81 1.74 1.4191 1 1 7 8 68.60 7.73 1.3680 2 0 6 8 68.73 7.37 1.3658 2 2 0 4 69.05 3.72 1.3602 1 0 8 8 75.49 1.48 1.2593 2 0 7 8 77.99 1.82 1.2251 1 0 9 8 78.23 5.66 1.2220 3 0 3 8 78.26 6.04 1.2216 3 1 0 8 81.78 1.78 1.1776 2 2 5 8 82.86 1.43 1.1651 3 1 3 16 87.35 3.42 1.1163 2 2 6 8 87.65 1.72 1.1133 1 0 10 8 87.77 3.38 1.1121 2 1 8 16 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.