Ca Cu2 La2 O6.037
      Fuertes A, Obradors X, Navarro J, Gomez-Romero P, Casan-Pastor N,
      Perez F, Fontcuberta J, Miravitlles C
      Rodriguez-Carvajal J, Martinez B
      Physica C 170 (1990) 153-160
      Oxygen excess and superconductivity at 45 K in La2 Ca Cu2 O6+y
      _cod_database_code 1006107
      _database_code_amcsd 0015020

      CELL PARAMETERS:    3.8282   3.8282  19.4498   90.000   90.000   90.000
      SPACE GROUP: I4/mmm    
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:    285.039
      Density (g/cm3):      6.309
      MAX. ABS. INTENSITY / VOLUME**2:      106.5449646    
      RIR:      5.499
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                18.24         11.03        4.8625    0   0   4         2
                23.69          3.93        3.7561    1   0   1         8
                27.05         32.88        3.2964    1   0   3         8
                27.52          2.93        3.2416    0   0   6         2
                32.82        100.00        2.7285    1   0   5         8
                33.09         76.83        2.7069    1   1   0         4
                34.39          4.68        2.6078    1   1   2         8
                36.97         10.54        2.4312    0   0   8         2
                40.10         28.88        2.2487    1   0   7         8
                43.56         18.40        2.0778    1   1   6         8
                46.70          3.54        1.9450    0   0  10         2
                47.50         42.49        1.9141    2   0   0         4
                48.36          9.16        1.8819    1   0   9         8
                50.45          8.10        1.8088    1   1   8         8
                51.30          2.39        1.7811    2   0   4         8
                55.52          7.79        1.6553    2   1   3        16
                55.77          1.50        1.6482    2   0   6         8
                56.80          7.01        1.6208    0   0  12         2
                57.40          3.25        1.6052    1   0  11         8
                58.43          3.64        1.5795    1   1  10         8
                58.94         31.02        1.5670    2   1   5        16
                61.67          7.13        1.5039    2   0   8         8
                63.86         11.24        1.4576    2   1   7        16
                67.34          8.43        1.3906    1   1  12         8
                68.82          3.28        1.3643    2   0  10         8
                69.44         10.46        1.3535    2   2   0         4
                70.13          4.84        1.3420    2   1   9        16
                76.01          1.33        1.2520    3   0   3         8
                77.11          9.19        1.2369    2   0  12         8
                77.18          1.01        1.2360    1   1  14         8
                77.63          2.17        1.2300    2   1  11        16
                78.96          5.56        1.2125    3   0   5         8
                79.11          8.59        1.2106    3   1   0         8
                81.37          2.60        1.1826    2   2   8         8
                83.33          2.17        1.1596    3   0   7         8
                85.65          2.91        1.1341    3   1   6        16
                87.88          1.39        1.1110    2   2  10         8
                89.11          1.11        1.0988    3   0   9         8
                89.38          7.08        1.0962    1   0  17         8
================================================================================