Ba2 Ca0.14 Co0.12 Cu2.88 O6.96 Y0.86 Suard E, Caignaert V, Maignan A, Bouree F, Raveau B Physica C 210 (1993) 164-172 Influence of thermal treatment on Y1-xCaxBa2Cu3-xCoxO7. A neutron diffraction study _cod_database_code 1001586 _database_code_amcsd 0015047 CELL PARAMETERS: 3.8618 3.8618 11.6910 90.000 90.000 90.000 SPACE GROUP: P4/mmm X-RAY WAVELENGTH: 1.541838 Cell Volume: 174.354 Density (g/cm3): 6.267 MAX. ABS. INTENSITY / VOLUME**2: 157.0610044 RIR: 8.160 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 15.16 2.27 5.8455 0 0 2 2 22.82 2.65 3.8970 0 0 3 2 23.03 5.20 3.8618 1 0 0 4 27.69 10.48 3.2221 1 0 2 8 32.64 100.00 2.7431 1 0 3 8 32.80 52.98 2.7307 1 1 0 4 36.31 2.58 2.4741 1 1 2 8 38.50 7.11 2.3382 0 0 5 2 38.63 6.79 2.3305 1 0 4 8 40.33 10.47 2.2363 1 1 3 8 46.61 7.61 1.9485 0 0 6 2 47.06 29.81 1.9309 2 0 0 4 51.45 4.37 1.7761 1 1 5 8 54.98 1.25 1.6701 0 0 7 2 55.48 2.61 1.6563 2 1 2 16 58.16 12.87 1.5861 1 1 6 8 58.45 31.54 1.5789 2 1 3 16 62.37 5.19 1.4889 2 0 5 8 62.46 2.51 1.4869 2 1 4 16 65.51 1.81 1.4248 1 1 7 8 68.40 7.63 1.3715 2 0 6 8 68.67 4.15 1.3668 1 0 8 8 68.75 7.42 1.3654 2 2 0 4 75.22 1.63 1.2632 2 0 7 8 77.53 1.63 1.2312 1 0 9 8 78.20 5.59 1.2223 3 0 3 8 78.29 6.16 1.2212 3 1 0 8 81.66 1.94 1.1791 2 2 5 8 82.84 1.32 1.1653 3 1 3 16 87.10 1.89 1.1189 1 0 10 8 87.17 3.34 1.1182 2 2 6 8 87.43 3.76 1.1156 2 1 8 16 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.