Bi2 Cu3 O16 Sr5 Pelloquin D, Maignan A, Caldes M, Hervieu M, Michel C, Raveau B Physica C 212 (1993) 199-205 The bismuth oxycarbonate Bi2Sr6-xCu3O10(CO3)2. A new 40K superconductor, second member of the series (Bi2Sr2CuO6)n(Sr2CuO2CO3)n' _cod_database_code 1001571 _database_code_amcsd 0015053 CELL PARAMETERS: 5.4690 5.4830 54.2600 90.000 90.000 90.000 SPACE GROUP: Fmmm X-RAY WAVELENGTH: 1.541838 Cell Volume: 1627.069 Density (g/cm3): 5.415 MAX. ABS. INTENSITY / VOLUME**2: 150.0112118 RIR: 9.021 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 3.26 100.00 27.1300 0 0 2 2 6.52 8.71 13.5650 0 0 4 2 13.05 8.78 6.7825 0 0 8 2 19.63 3.93 4.5217 0 0 12 2 22.95 2.47 3.8757 0 0 14 2 23.50 5.52 3.7863 1 1 3 8 24.41 13.48 3.6469 1 1 5 8 25.72 6.74 3.4640 1 1 7 8 26.28 8.61 3.3912 0 0 16 2 27.37 29.69 3.2580 1 1 9 8 29.32 24.94 3.0458 1 1 11 8 29.64 6.30 3.0144 0 0 18 2 31.52 25.62 2.8387 1 1 13 8 32.66 24.33 2.7415 0 2 0 2 32.75 24.15 2.7345 2 0 0 2 32.84 2.96 2.7276 0 2 2 4 32.92 2.94 2.7207 2 0 2 4 33.02 3.36 2.7130 0 0 20 2 33.34 1.32 2.6872 0 2 4 4 33.43 1.31 2.6806 2 0 4 4 33.91 11.82 2.6433 1 1 15 8 36.43 3.88 2.4664 0 0 22 2 38.40 1.47 2.3443 0 2 12 4 38.47 1.46 2.3399 2 0 12 4 42.40 7.58 2.1320 0 2 16 4 42.47 7.54 2.1287 2 0 16 4 44.68 4.66 2.0282 0 2 18 4 44.75 4.64 2.0253 2 0 18 4 45.00 5.51 2.0147 1 1 23 8 46.88 4.07 1.9379 0 0 28 2 46.93 22.71 1.9361 2 2 0 4 47.06 1.24 1.9311 2 2 2 8 47.13 2.44 1.9284 0 2 20 4 47.19 2.43 1.9259 2 0 20 4 48.06 3.87 1.8933 1 1 25 8 48.92 1.29 1.8617 2 2 8 8 49.73 1.58 1.8336 0 2 22 4 49.79 1.57 1.8315 2 0 22 4 51.21 2.66 1.7837 1 1 27 8 51.34 1.20 1.7798 2 2 12 8 53.54 1.60 1.7117 1 3 5 8 53.65 1.59 1.7083 3 1 5 8 54.47 2.98 1.6847 1 1 29 8 54.58 4.18 1.6814 2 2 16 8 55.13 4.11 1.6659 1 3 9 8 55.24 4.08 1.6628 3 1 9 8 56.25 3.58 1.6354 1 3 11 8 56.36 3.55 1.6324 3 1 11 8 56.49 3.37 1.6290 2 2 18 8 57.58 3.75 1.6009 1 3 13 8 57.69 3.73 1.5981 3 1 13 8 58.31 2.36 1.5824 0 2 28 4 58.36 2.35 1.5811 2 0 28 4 58.57 1.95 1.5759 2 2 20 8 59.10 1.79 1.5632 1 3 15 8 59.21 1.77 1.5606 3 1 15 8 60.82 3.04 1.5229 2 2 22 8 61.53 1.58 1.5072 0 0 36 2 66.99 1.57 1.3969 1 3 23 8 67.09 1.57 1.3950 3 1 23 8 68.44 2.78 1.3707 0 4 0 2 68.51 3.82 1.3696 2 2 28 8 68.64 2.75 1.3672 4 0 0 2 69.38 1.10 1.3545 1 3 25 8 69.48 1.09 1.3528 3 1 25 8 71.42 1.37 1.3208 0 2 36 4 71.47 1.37 1.3200 2 0 36 4 74.64 1.13 1.2716 1 3 29 8 74.74 1.12 1.2702 3 1 29 8 75.30 1.26 1.2621 3 3 9 8 76.25 1.24 1.2487 3 3 11 8 77.39 1.51 1.2331 3 3 13 8 77.52 1.03 1.2314 2 2 34 8 77.97 2.78 1.2254 2 4 0 4 78.11 2.77 1.2235 4 2 0 4 80.81 2.49 1.1893 2 2 36 8 83.97 1.26 1.1525 2 4 16 8 84.08 1.97 1.1513 1 1 45 8 84.11 1.25 1.1509 4 2 16 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.