Ba4 Cu2 Hg O10 Tl2 Martin C, Huve M, Van Tendeloo G, Maignan A, Michel C, Hervieu M, Raveau B Physica C 212 (1993) 274-278 A mercury-based superconducting cuprate, intergrowth of the 2201 and 1201 structures Tl2HgBa4Cu2O10+y _cod_database_code 1001575 _database_code_amcsd 0015055 CELL PARAMETERS: 3.8584 3.8584 42.2031 90.000 90.000 90.000 SPACE GROUP: I4/mmm X-RAY WAVELENGTH: 1.541838 Cell Volume: 628.288 Density (g/cm3): 7.641 MAX. ABS. INTENSITY / VOLUME**2: 311.8820835 RIR: 13.290 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 4.19 20.83 21.1015 0 0 2 2 8.38 6.92 10.5508 0 0 4 2 12.58 1.12 7.0338 0 0 6 2 16.81 1.53 5.2754 0 0 8 2 23.91 2.02 3.7210 1 0 3 8 25.32 1.52 3.5169 0 0 12 2 25.38 23.43 3.5091 1 0 5 8 29.63 5.71 3.0145 0 0 14 2 29.99 100.00 2.9795 1 0 9 8 32.83 54.82 2.7283 1 1 0 4 32.92 1.52 2.7206 1 0 11 8 33.11 1.19 2.7058 1 1 2 8 33.94 4.94 2.6414 1 1 4 8 38.39 12.43 2.3446 0 0 18 2 41.91 2.93 2.1557 1 1 12 8 43.34 4.43 2.0877 1 0 17 8 44.80 10.27 2.0228 1 1 14 8 47.11 21.98 1.9292 2 0 0 4 51.26 2.39 1.7824 1 0 21 8 51.38 15.80 1.7782 1 1 18 8 54.26 5.34 1.6906 2 1 5 16 55.01 1.11 1.6692 1 1 20 8 55.45 6.78 1.6571 1 0 23 8 56.64 3.49 1.6249 2 0 14 8 56.71 1.56 1.6232 0 0 26 2 56.86 29.28 1.6194 2 1 9 16 62.33 9.98 1.4897 2 0 18 8 64.30 4.01 1.4487 1 0 27 8 65.93 2.23 1.4169 2 1 17 16 67.10 2.57 1.3950 1 1 26 8 68.82 5.83 1.3642 2 2 0 4 72.15 1.41 1.3092 2 1 21 16 75.66 4.65 1.2570 2 1 23 16 76.68 1.32 1.2428 2 2 14 8 76.73 2.17 1.2420 2 0 26 8 76.86 5.32 1.2403 3 0 9 8 78.37 6.50 1.2201 3 1 0 8 80.97 1.51 1.1874 1 1 32 8 81.66 3.99 1.1791 2 2 18 8 83.44 3.50 1.1584 2 1 27 16 84.11 2.55 1.1509 1 0 35 8 85.94 2.44 1.1310 3 1 14 16 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.