Bi0.5 Cu Hg0.5 La0.5 O5 Sr1.5 Pelloquin D, Michel C, Van Tendeloo G, Maignan A, Hervieu M, Raveau B Physica C 214 (1993) 87-92 A new "1201" mercury cuprate. The 27K-superconductor Hg0.5Bi0.5Sr2-xLaxCuO5-d _cod_database_code 1001573 _database_code_amcsd 0015056 CELL PARAMETERS: 3.7753 3.7753 8.8765 90.000 90.000 90.000 SPACE GROUP: P4/mmm X-RAY WAVELENGTH: 1.541838 Cell Volume: 126.516 Density (g/cm3): 7.207 MAX. ABS. INTENSITY / VOLUME**2: 218.2618018 RIR: 9.860 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 9.96 8.00 8.8765 0 0 1 2 20.01 7.59 4.4383 0 0 2 2 23.57 5.65 3.7753 1 0 0 4 25.64 32.92 3.4741 1 0 1 8 30.21 10.97 2.9588 0 0 3 2 31.10 100.00 2.8757 1 0 2 8 33.57 63.37 2.6695 1 1 0 4 35.10 8.25 2.5564 1 1 1 8 39.39 1.25 2.2876 1 1 2 8 40.66 14.30 2.2191 0 0 4 2 45.78 20.53 1.9821 1 1 3 8 47.53 7.62 1.9131 1 0 4 8 48.21 26.23 1.8877 2 0 0 4 52.69 2.18 1.7371 2 0 2 8 53.71 16.82 1.7065 1 1 4 8 54.34 1.15 1.6884 2 1 0 8 55.39 7.13 1.6586 2 1 1 16 57.35 10.68 1.6065 1 0 5 8 57.95 6.17 1.5914 2 0 3 8 58.49 29.26 1.5780 2 1 2 16 62.81 1.85 1.4794 0 0 6 2 64.85 11.31 1.4378 2 0 4 8 68.07 2.75 1.3774 1 0 6 8 70.02 4.13 1.3437 2 1 4 16 70.56 6.67 1.3348 2 2 0 4 73.13 3.11 1.2940 1 1 6 8 76.45 1.22 1.2460 3 0 1 8 78.12 7.31 1.2234 2 1 5 16 78.63 2.22 1.2167 2 2 3 8 79.10 5.27 1.2107 3 0 2 8 80.44 7.03 1.1939 3 1 0 8 82.92 2.87 1.1644 2 0 6 8 84.61 2.86 1.1454 1 1 7 8 84.75 4.49 1.1438 2 2 4 8 87.71 2.54 1.1127 2 1 6 16 88.27 4.40 1.1071 3 1 3 16 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.