Ba2 Co0.38 Cu2.62 O6.91 Y Renevier H, Hodeau J, Marezio M, Santoro A Physica C 220 (1994) 143-159 Electron- and powder neutron-diffraction studies of Y Ba2 (Cu1-y Coy)3 O6+x with 0.05< y< 0.33 _cod_database_code 1008669 _database_code_amcsd 0016555 CELL PARAMETERS: 3.8772 3.8772 11.7352 90.000 90.000 90.000 SPACE GROUP: P4/mmm X-RAY WAVELENGTH: 1.541838 Cell Volume: 176.411 Density (g/cm3): 6.240 MAX. ABS. INTENSITY / VOLUME**2: 147.4372597 RIR: 7.694 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 7.53 9.01 11.7352 0 0 1 2 15.10 3.90 5.8676 0 0 2 2 22.73 3.93 3.9117 0 0 3 2 22.94 6.37 3.8772 1 0 0 4 27.57 13.91 3.2348 1 0 2 8 32.52 100.00 2.7537 1 0 3 8 32.66 60.39 2.7416 1 1 0 4 36.16 1.97 2.4838 1 1 2 8 38.35 7.71 2.3470 0 0 5 2 38.48 13.08 2.3395 1 0 4 8 40.17 9.32 2.2451 1 1 3 8 45.27 1.60 2.0031 1 1 4 8 46.43 5.39 1.9559 0 0 6 2 46.86 30.65 1.9386 2 0 0 4 51.24 5.99 1.7829 1 1 5 8 52.70 1.24 1.7370 2 0 3 8 52.80 1.10 1.7339 2 1 0 8 54.75 2.22 1.6765 0 0 7 2 55.24 3.36 1.6629 2 1 2 16 57.92 10.95 1.5922 1 1 6 8 58.20 31.54 1.5852 2 1 3 16 60.13 2.45 1.5388 1 0 7 8 62.10 5.79 1.4947 2 0 5 8 62.19 4.98 1.4927 2 1 4 16 65.23 3.13 1.4302 1 1 7 8 68.10 5.52 1.3769 2 0 6 8 68.37 4.57 1.3720 1 0 8 8 68.44 7.72 1.3708 2 2 0 4 74.88 2.87 1.2681 2 0 7 8 77.84 5.66 1.2272 3 0 3 8 77.92 6.88 1.2261 3 1 0 8 79.53 1.75 1.2052 2 1 7 16 81.28 2.20 1.1837 2 2 5 8 82.44 1.24 1.1700 3 1 3 16 86.69 2.60 1.1232 1 0 10 8 86.75 2.44 1.1225 2 2 6 8 87.00 4.09 1.1199 2 1 8 16 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.