Ba2 Co0.554 Cu2.446 O7.12 Y Renevier H, Hodeau J, Marezio M, Santoro A Physica C 220 (1994) 143-159 Electron- and powder neutron-diffraction studies of Y Ba2 (Cu1-y Coy)3 O6+x with 0.05< y< 0.33 _cod_database_code 1008670 _database_code_amcsd 0016556 CELL PARAMETERS: 3.8850 3.8850 11.7055 90.000 90.000 90.000 SPACE GROUP: P4/mmm X-RAY WAVELENGTH: 1.541838 Cell Volume: 176.674 Density (g/cm3): 6.255 MAX. ABS. INTENSITY / VOLUME**2: 150.2549888 RIR: 7.822 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 7.55 6.53 11.7055 0 0 1 2 15.14 3.79 5.8527 0 0 2 2 22.79 4.12 3.9018 0 0 3 2 22.89 6.39 3.8850 1 0 0 4 27.56 11.78 3.2368 1 0 2 8 32.52 100.00 2.7530 1 0 3 8 32.60 59.14 2.7471 1 1 0 4 33.51 1.01 2.6744 1 1 1 8 36.12 1.88 2.4868 1 1 2 8 38.45 7.07 2.3411 0 0 5 2 38.51 10.82 2.3374 1 0 4 8 40.14 9.73 2.2462 1 1 3 8 45.28 1.16 2.0029 1 1 4 8 46.55 6.02 1.9509 0 0 6 2 46.77 30.08 1.9425 2 0 0 4 51.27 5.47 1.7818 1 1 5 8 52.63 1.32 1.7389 2 0 3 8 52.68 1.11 1.7374 2 1 0 8 54.91 1.93 1.6722 0 0 7 2 55.14 2.87 1.6656 2 1 2 16 57.98 11.98 1.5906 1 1 6 8 58.12 31.70 1.5872 2 1 3 16 60.25 1.79 1.5360 1 0 7 8 62.09 5.33 1.4949 2 0 5 8 62.13 4.14 1.4940 2 1 4 16 65.33 2.59 1.4284 1 1 7 8 68.12 6.20 1.3765 2 0 6 8 68.29 7.58 1.3736 2 2 0 4 68.53 4.33 1.3693 1 0 8 8 74.93 2.51 1.2673 2 0 7 8 77.69 5.69 1.2291 3 0 3 8 77.73 6.75 1.2285 3 1 0 8 79.56 1.29 1.2048 2 1 7 16 81.19 2.02 1.1847 2 2 5 8 82.28 1.31 1.1718 3 1 3 16 86.69 2.74 1.1231 2 2 6 8 86.92 2.40 1.1208 1 0 10 8 87.07 3.91 1.1192 2 1 8 16 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.