LiTi2O4 Moshopoulou E, Bordet P, Sulpice A, Capponi J Physica C 235 (1994) 747-748 Evolution of structure and superconductivity of Li(1-x)Ti2O4 single crystals without Ti cation disorder Note: Spinel structure _cod_database_code 1008791 _database_code_amcsd 0016663 CELL PARAMETERS: 8.4210 8.4210 8.4210 90.000 90.000 90.000 SPACE GROUP: Fd3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 597.160 Density (g/cm3): 3.712 MAX. ABS. INTENSITY / VOLUME**2: 49.09969753 RIR: 4.307 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.25 100.00 4.8619 1 1 1 8 35.35 43.75 2.5390 3 1 1 24 36.98 5.42 2.4309 2 2 2 8 42.96 57.55 2.1052 4 0 0 6 47.04 7.70 1.9319 3 3 1 24 56.81 18.01 1.6206 5 1 1 24 56.81 1.29 1.6206 3 3 3 8 62.38 32.67 1.4886 4 4 0 12 65.59 11.95 1.4234 5 3 1 48 73.78 4.08 1.2842 5 3 3 24 74.78 3.79 1.2695 6 2 2 24 78.73 7.73 1.2155 4 4 4 8 81.65 1.30 1.1792 7 1 1 24 81.65 4.81 1.1792 5 5 1 24 89.37 2.28 1.0963 7 3 1 48 89.37 3.62 1.0963 5 5 3 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.