Ba2 Cu Hg0.88 O4.87 S0.18 Bordet P, Loureiro S, LeFloch S, Capponi J, Chaillout C, Chenavas J, Tholence J, Antipov E, Radaelli P, Marezio M Physica C 282 (1997) 65-68 High pressure synthesis and structure of the superconducting mercury cuprates (Hg(1-x) M(x)) Ba2 Ca(n-1) Cu(n) O(2+2n+d) with M= C, S _cod_database_code 1008817 _database_code_amcsd 0016687 CELL PARAMETERS: 3.8986 3.8986 9.2466 90.000 90.000 90.000 SPACE GROUP: P4/mmm X-RAY WAVELENGTH: 1.541838 Cell Volume: 140.540 Density (g/cm3): 7.069 MAX. ABS. INTENSITY / VOLUME**2: 246.9471834 RIR: 11.374 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 24.78 29.33 3.5924 1 0 1 8 28.97 8.73 3.0822 0 0 3 2 29.98 100.00 2.9804 1 0 2 8 32.48 57.05 2.7567 1 1 0 4 33.93 3.05 2.6418 1 1 1 8 37.19 3.15 2.4179 1 0 3 8 38.96 11.68 2.3117 0 0 4 2 44.07 16.30 2.0548 1 1 3 8 45.62 3.06 1.9884 1 0 4 8 46.59 23.39 1.9493 2 0 0 4 51.60 13.60 1.7713 1 1 4 8 53.48 6.29 1.7133 2 1 1 16 54.95 11.92 1.6709 1 0 5 8 55.80 4.85 1.6475 2 0 3 8 56.40 29.62 1.6314 2 1 2 16 60.03 1.34 1.5411 0 0 6 2 62.31 9.21 1.4902 2 0 4 8 65.08 2.61 1.4332 1 0 6 8 67.26 1.80 1.3920 2 1 4 16 68.01 6.07 1.3784 2 2 0 4 69.93 2.07 1.3452 1 1 6 8 73.60 1.10 1.2869 3 0 1 8 74.85 8.15 1.2686 2 1 5 16 75.57 1.81 1.2583 2 2 3 8 76.08 5.39 1.2511 3 0 2 8 77.41 6.40 1.2328 3 1 0 8 79.24 1.93 1.2089 2 0 6 8 80.65 2.95 1.1912 1 1 7 8 81.26 3.67 1.1839 2 2 4 8 83.77 2.33 1.1547 2 1 6 16 84.67 3.55 1.1447 3 1 3 16 88.16 2.62 1.1081 1 0 8 8 89.66 1.64 1.0935 2 0 7 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.