Ca0.03 Cu La1.97 O4 Rial C, Moran E, Alario-Franco M, Amador U, Martinez J, Rodriguez-Carvajal J, Andersen N Physica C 297 (1998) 277-293 Effects of extra oxygen on the structure and superconductivity of La2-xCaxCuO4+y prepared by chemical oxidation _cod_database_code 1006173 _database_code_amcsd 0015082 CELL PARAMETERS: 5.3513 5.3907 13.1603 90.000 90.000 90.000 SPACE GROUP: Bmab X-RAY WAVELENGTH: 1.541838 Cell Volume: 379.638 Density (g/cm3): 7.039 MAX. ABS. INTENSITY / VOLUME**2: 177.8515280 RIR: 8.227 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 13.46 3.72 6.5802 0 0 2 2 24.39 19.38 3.6489 1 1 1 8 27.10 11.00 3.2901 0 0 4 2 31.15 100.00 2.8713 1 1 3 8 33.24 32.35 2.6953 0 2 0 2 33.49 32.28 2.6756 2 0 0 2 41.16 10.38 2.1934 0 0 6 2 41.75 21.50 2.1633 1 1 5 8 43.40 11.46 2.0850 0 2 4 4 43.60 11.36 2.0758 2 0 4 4 47.91 29.18 1.8989 2 2 0 4 53.89 4.81 1.7013 0 2 6 4 54.06 4.86 1.6963 2 0 6 4 54.30 1.82 1.6893 1 3 1 8 54.46 8.92 1.6849 1 1 7 8 54.64 1.73 1.6796 3 1 1 8 55.89 4.15 1.6450 0 0 8 2 55.91 4.91 1.6446 2 2 4 8 58.09 14.70 1.5879 1 3 3 8 58.42 14.07 1.5798 3 1 3 8 64.96 7.91 1.4356 2 2 6 8 65.24 4.23 1.4301 1 3 5 8 65.55 4.34 1.4242 3 1 5 8 66.60 3.01 1.4042 0 2 8 4 66.75 2.94 1.4014 2 0 8 4 69.78 3.54 1.3477 0 4 0 2 70.37 3.62 1.3378 4 0 0 2 75.28 2.73 1.2623 1 3 7 8 75.57 2.74 1.2583 3 1 7 8 76.64 5.45 1.2434 2 2 8 8 78.67 5.11 1.2163 3 3 3 8 79.66 3.34 1.2036 2 4 0 4 80.08 3.43 1.1983 4 2 0 4 84.35 1.49 1.1482 0 4 6 4 84.91 1.55 1.1421 4 0 6 4 85.00 6.49 1.1411 1 1 11 8 85.02 1.68 1.1408 3 3 5 8 86.00 1.95 1.1304 2 4 4 8 86.42 1.96 1.1260 4 2 4 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.