Ca0.08 Cu La1.92 O4 Rial C, Moran E, Alario-Franco M, Amador U, Martinez J, Rodriguez-Carvajal J, Andersen N Physica C 297 (1998) 277-293 Effects of extra oxygen on the structure and superconductivity of La2-xCaxCuO4+y prepared by chemical oxidation _cod_database_code 1006175 _database_code_amcsd 0015084 CELL PARAMETERS: 5.3456 5.3673 13.1698 90.000 90.000 90.000 SPACE GROUP: Bmab X-RAY WAVELENGTH: 1.541838 Cell Volume: 377.861 Density (g/cm3): 6.983 MAX. ABS. INTENSITY / VOLUME**2: 175.0487355 RIR: 8.163 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 13.45 3.72 6.5849 0 0 2 2 24.45 18.13 3.6400 1 1 1 8 27.08 10.50 3.2924 0 0 4 2 31.19 100.00 2.8677 1 1 3 8 33.39 32.10 2.6837 0 2 0 2 33.53 32.09 2.6728 2 0 0 2 41.12 10.84 2.1950 0 0 6 2 41.77 20.85 2.1625 1 1 5 8 43.51 11.13 2.0802 0 2 4 4 43.62 11.09 2.0751 2 0 4 4 48.04 29.10 1.8938 2 2 0 4 53.97 5.02 1.6990 0 2 6 4 54.06 5.05 1.6963 2 0 6 4 54.46 8.79 1.6850 1 1 7 8 54.54 1.67 1.6827 1 3 1 8 54.72 1.62 1.6773 3 1 1 8 55.85 4.06 1.6462 0 0 8 2 56.02 4.66 1.6416 2 2 4 8 58.31 14.40 1.5825 1 3 3 8 58.49 14.05 1.5781 3 1 3 8 65.05 8.26 1.4339 2 2 6 8 65.43 4.13 1.4263 1 3 5 8 65.60 4.20 1.4231 3 1 5 8 66.65 2.84 1.4032 0 2 8 4 66.73 2.81 1.4017 2 0 8 4 70.13 3.55 1.3418 0 4 0 2 70.46 3.60 1.3364 4 0 0 2 75.45 2.68 1.2600 1 3 7 8 75.61 2.69 1.2577 3 1 7 8 76.70 5.27 1.2424 2 2 8 8 78.89 5.03 1.2133 3 3 3 8 80.01 3.36 1.1992 2 4 0 4 80.25 3.42 1.1963 4 2 0 4 84.66 1.57 1.1448 0 4 6 4 84.96 6.44 1.1416 1 1 11 8 84.97 1.61 1.1415 4 0 6 4 85.24 1.64 1.1385 3 3 5 8 86.34 1.89 1.1268 2 4 4 8 86.57 1.90 1.1244 4 2 4 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.