Ca0.1 Cu La1.9 O4 Rial C, Moran E, Alario-Franco M, Amador U, Martinez J, Rodriguez-Carvajal J, Andersen N Physica C 297 (1998) 277-293 Effects of extra oxygen on the structure and superconductivity of La2-xCaxCuO4+y prepared by chemical oxidation _cod_database_code 1006176 _database_code_amcsd 0015085 CELL PARAMETERS: 5.3440 5.3580 13.1752 90.000 90.000 90.000 SPACE GROUP: Bmab X-RAY WAVELENGTH: 1.541838 Cell Volume: 377.247 Density (g/cm3): 6.962 MAX. ABS. INTENSITY / VOLUME**2: 173.6686572 RIR: 8.122 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 13.44 3.78 6.5876 0 0 2 2 24.48 17.63 3.6367 1 1 1 8 27.07 10.32 3.2938 0 0 4 2 31.20 100.00 2.8666 1 1 3 8 33.45 32.05 2.6790 0 2 0 2 33.54 32.03 2.6720 2 0 0 2 41.11 11.07 2.1959 0 0 6 2 41.77 20.64 2.1623 1 1 5 8 43.55 11.07 2.0783 0 2 4 4 43.62 11.03 2.0751 2 0 4 4 48.09 29.17 1.8919 2 2 0 4 53.99 5.11 1.6983 0 2 6 4 54.06 5.13 1.6965 2 0 6 4 54.45 8.72 1.6852 1 1 7 8 54.63 1.61 1.6801 1 3 1 8 54.75 1.58 1.6766 3 1 1 8 55.82 4.04 1.6469 0 0 8 2 56.06 4.58 1.6405 2 2 4 8 58.39 14.29 1.5804 1 3 3 8 58.51 14.06 1.5775 3 1 3 8 65.08 8.43 1.4333 2 2 6 8 65.51 4.11 1.4249 1 3 5 8 65.62 4.15 1.4228 3 1 5 8 66.66 2.78 1.4030 0 2 8 4 66.72 2.76 1.4020 2 0 8 4 70.27 3.58 1.3395 0 4 0 2 70.48 3.60 1.3360 4 0 0 2 75.51 2.67 1.2591 1 3 7 8 75.61 2.67 1.2576 3 1 7 8 76.72 5.22 1.2422 2 2 8 8 78.98 5.00 1.2122 3 3 3 8 80.15 3.38 1.1975 2 4 0 4 80.30 3.42 1.1956 4 2 0 4 84.78 1.61 1.1435 0 4 6 4 84.93 6.44 1.1419 1 1 11 8 84.98 1.64 1.1414 4 0 6 4 85.32 1.63 1.1376 3 3 5 8 86.47 1.89 1.1254 2 4 4 8 86.62 1.89 1.1238 4 2 4 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.