Ca0.12 Cu La1.88 O4 Rial C, Moran E, Alario-Franco M, Amador U, Martinez J, Rodriguez-Carvajal J, Andersen N Physica C 297 (1998) 277-293 Effects of extra oxygen on the structure and superconductivity of La2-xCaxCuO4+y prepared by chemical oxidation _cod_database_code 1006177 _database_code_amcsd 0015086 CELL PARAMETERS: 5.3491 5.3491 13.1846 90.000 90.000 90.000 SPACE GROUP: F4/mmm X-RAY WAVELENGTH: 1.541838 Cell Volume: 377.249 Density (g/cm3): 6.922 MAX. ABS. INTENSITY / VOLUME**2: 172.2591756 RIR: 8.104 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 13.43 3.64 6.5923 0 0 2 2 24.48 17.01 3.6357 1 1 1 8 27.05 10.13 3.2961 0 0 4 2 31.20 100.00 2.8668 1 1 3 8 33.51 32.10 2.6746 0 2 0 2 33.51 32.10 2.6746 2 0 0 2 41.08 11.38 2.1974 0 0 6 2 41.76 20.16 2.1631 1 1 5 8 43.58 10.92 2.0769 0 2 4 4 43.58 10.92 2.0769 2 0 4 4 48.11 29.20 1.8912 2 2 0 4 54.01 5.28 1.6979 2 0 6 4 54.01 5.28 1.6979 0 2 6 4 54.42 8.65 1.6860 1 1 7 8 54.71 1.53 1.6778 3 1 1 8 54.71 1.53 1.6778 1 3 1 8 55.78 3.98 1.6481 0 0 8 2 56.06 4.50 1.6404 2 2 4 8 58.46 14.09 1.5786 3 1 3 8 58.46 14.09 1.5786 1 3 3 8 65.07 8.69 1.4334 2 2 6 8 65.57 4.06 1.4238 3 1 5 8 65.57 4.06 1.4238 1 3 5 8 66.66 2.67 1.4031 0 2 8 4 66.66 2.67 1.4031 2 0 8 4 70.41 3.61 1.3373 0 4 0 2 70.41 3.61 1.3373 4 0 0 2 75.55 2.65 1.2585 3 1 7 8 75.55 2.65 1.2585 1 3 7 8 76.70 5.10 1.2425 2 2 8 8 79.01 4.96 1.2119 3 3 3 8 80.26 3.43 1.1961 2 4 0 4 80.26 3.43 1.1961 4 2 0 4 84.86 6.40 1.1426 1 1 11 8 84.88 1.68 1.1424 0 4 6 4 84.88 1.68 1.1424 4 0 6 4 85.34 1.61 1.1375 3 3 5 8 86.57 1.87 1.1244 4 2 4 8 86.57 1.87 1.1244 2 4 4 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.