Ca0.08 Cu La1.92 O4 Rial C, Moran E, Alario-Franco M, Amador U, Martinez J, Rodriguez-Carvajal J, Andersen N Physica C 297 (1998) 277-293 Effects of extra oxygen on the structure and superconductivity of La2-xCaxCuO4+y prepared by chemical oxidation _cod_database_code 1006180 _database_code_amcsd 0015089 CELL PARAMETERS: 5.3271 5.3793 13.1327 90.000 90.000 90.000 SPACE GROUP: Bmab X-RAY WAVELENGTH: 1.541838 Cell Volume: 376.332 Density (g/cm3): 7.017 MAX. ABS. INTENSITY / VOLUME**2: 174.6168142 RIR: 8.103 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 13.48 4.25 6.5663 0 0 2 2 24.47 18.56 3.6371 1 1 1 8 27.16 10.72 3.2832 0 0 4 2 31.24 100.00 2.8632 1 1 3 8 33.31 32.24 2.6897 0 2 0 2 33.65 31.96 2.6635 2 0 0 2 41.25 10.57 2.1888 0 0 6 2 41.86 21.54 2.1579 1 1 5 8 43.50 11.43 2.0806 0 2 4 4 43.76 11.28 2.0685 2 0 4 4 48.08 29.20 1.8926 2 2 0 4 54.01 4.83 1.6977 0 2 6 4 54.24 4.86 1.6911 2 0 6 4 54.44 1.75 1.6854 1 3 1 8 54.60 8.63 1.6810 1 1 7 8 54.90 1.65 1.6725 3 1 1 8 56.02 4.18 1.6416 0 0 8 2 56.09 4.75 1.6397 2 2 4 8 58.24 14.70 1.5842 1 3 3 8 58.67 13.96 1.5735 3 1 3 8 65.16 8.00 1.4316 2 2 6 8 65.41 4.24 1.4268 1 3 5 8 65.82 4.32 1.4190 3 1 5 8 66.76 2.99 1.4012 0 2 8 4 66.96 2.92 1.3975 2 0 8 4 69.95 3.55 1.3448 0 4 0 2 70.74 3.59 1.3318 4 0 0 2 75.48 2.64 1.2595 1 3 7 8 75.86 2.64 1.2541 3 1 7 8 76.88 5.48 1.2401 2 2 8 8 78.97 5.09 1.2124 3 3 3 8 79.91 3.32 1.2005 2 4 0 4 80.47 3.39 1.1935 4 2 0 4 84.57 1.51 1.1458 0 4 6 4 85.23 6.49 1.1386 1 1 11 8 85.31 1.56 1.1377 4 0 6 4 85.35 1.68 1.1373 3 3 5 8 86.28 1.93 1.1275 2 4 4 8 86.83 1.93 1.1217 4 2 4 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.