Ca0.1 Cu La1.9 O4 Rial C, Moran E, Alario-Franco M, Amador U, Martinez J, Rodriguez-Carvajal J, Andersen N Physica C 297 (1998) 277-293 Effects of extra oxygen on the structure and superconductivity of La2-xCaxCuO4+y prepared by chemical oxidation _cod_database_code 1006181 _database_code_amcsd 0015090 CELL PARAMETERS: 5.3239 5.3709 13.1446 90.000 90.000 90.000 SPACE GROUP: Bmab X-RAY WAVELENGTH: 1.541838 Cell Volume: 375.858 Density (g/cm3): 6.991 MAX. ABS. INTENSITY / VOLUME**2: 172.8644711 RIR: 8.052 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 13.47 4.33 6.5723 0 0 2 2 24.50 18.09 3.6337 1 1 1 8 27.14 10.63 3.2861 0 0 4 2 31.25 100.00 2.8626 1 1 3 8 33.37 32.19 2.6855 0 2 0 2 33.67 31.96 2.6620 2 0 0 2 41.21 10.75 2.1908 0 0 6 2 41.85 21.50 2.1585 1 1 5 8 43.52 11.33 2.0794 0 2 4 4 43.76 11.23 2.0685 2 0 4 4 48.13 29.20 1.8905 2 2 0 4 54.02 4.90 1.6975 0 2 6 4 54.23 4.94 1.6916 2 0 6 4 54.53 1.67 1.6830 1 3 1 8 54.57 8.56 1.6818 1 1 7 8 54.94 1.60 1.6714 3 1 1 8 55.96 4.18 1.6431 0 0 8 2 56.13 4.67 1.6387 2 2 4 8 58.31 14.51 1.5824 1 3 3 8 58.70 13.94 1.5727 3 1 3 8 65.18 8.11 1.4313 2 2 6 8 65.47 4.23 1.4257 1 3 5 8 65.83 4.31 1.4186 3 1 5 8 66.74 2.96 1.4015 0 2 8 4 66.92 2.90 1.3982 2 0 8 4 70.08 3.54 1.3427 0 4 0 2 70.79 3.59 1.3310 4 0 0 2 75.52 2.60 1.2590 1 3 7 8 75.86 2.62 1.2541 3 1 7 8 76.87 5.43 1.2402 2 2 8 8 79.06 5.03 1.2112 3 3 3 8 80.04 3.31 1.1988 2 4 0 4 80.55 3.38 1.1925 4 2 0 4 84.66 1.53 1.1448 0 4 6 4 85.16 6.51 1.1394 1 1 11 8 85.33 1.58 1.1375 4 0 6 4 85.43 1.67 1.1365 3 3 5 8 86.39 1.89 1.1262 2 4 4 8 86.90 1.91 1.1210 4 2 4 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.